No abstract

The purpose of this study was to investigate the effect of the output energy of laser welding and welding methods on the joint strength of cobalt-chromium (Co-Cr) alloy. Two types of cast Co-Cr plates were prepared, and transverse sections were made at the center of the plate. The cut surfaces were butted against one another, and the joints welded with a laser-welding machine at several levels of output energy with the use of two methods. The fracture force required to break specimens was determined by means of tensile testing. For the 0.5-mm-thick specimens, the force required to break the 0.5-mm laser-welded specimens at currents of 270 and 300 A was not statistically different (p > 0.05) from the results for the nonwelded control specimens. The force required to break the 1.0-mm specimens double-welded at a current of 270 A was the highest value among the 1.0-mm laser-welded specimens. The results suggested that laser welding under the appropriate conditions improved the joint strength of cobalt- chromium alloy.

This study investigated the effect of surface preparation on the Nd:YAG laser penetration into cast titanium and gold alloy. Cast blocks of each metal were given four different surface preparations: (i) coloured with black marker; (ii) air-abraded with 50 microm Al2O3; (iii) ground with SiC points and (iv) polished with 1 microm Al2O3 (mirror-polished). Two blocks with each of the surface preparations were abutted and laser-welded at their interface using the voltages of 210-260 V in increments of 10 V. After the welded blocks were mechanically separated, the laser penetration was measured using computer graphics. Regardless of the surface preparation, an increase in voltage increased the laser penetration for both metals. The laser penetration into titanium prepared with black marker and air-abrasion was significantly deeper than into the titanium ground with SiC points and mirror-polished. Although there were no statistical differences in penetration among the surface preparations for the gold alloy, the penetration in the mirror-polished specimens was shallower than any of the other preparation methods at higher voltages of 240-260 V. The results obtained in this study suggested that broken metal frameworks with finished surfaces should be painted with black marker or air-abraded before laser welding.

No abstract

The purpose of this study was to evaluate the effects of disinfectants on the bond strength of resin to dentine. The surface of bovine dentine was exposed to formaldehyde (FA) aqueous solutions, glutaraldehyde (GA) aqueous solutions, 2-hydroxyethyl methacrylate aqueous solutions (HEMA), a commercially available dentine primer (Gluma CPS desensitizer, GLUMA), isotonic sodium chloride solution (IS), and distilled water (DW), and placed in a humidor (HU) at 37 degrees C, or non-stored (baseline). All dentine surfaces were conditioned with a 10% citric acid and 3% ferric chloride solution (10-3 liquid), and then bonded to an acrylic rod with a self-curing adhesive resin (Super-Bond C&B). The mean tensile bond strengths determined 24 h after bonding were compared by analysis of variance (ANOVA) and Fisher's protected LSD test (n=5, P < or = 0.05). The exposure of dentine to IS, DW and HU for both 48 and 168 h resulted in a decrease in bond strength when compared with the baseline. The highest bond strengths after 168 h of exposure were obtained with 5% GA, 10% HEMA, and GLUMA, the values of which were equivalent to baseline and were significantly higher than that of FA. It is concluded that disinfectant pre-treatment with 5% GA or GLUMA stabilizes the bonding of tri-n-butylborane (TBB) initiated luting agent to bovine dentine conditioned with 10-3 liquid.