(1) Background: An ideal bond strength between endodontic posts and root canal dentin is essential for optimal retention and good prognosis. This study aimed to evaluate the push-out bond strength (PBS) of prefabricated fiber and metal posts, luted with resin cement to natural dentin. (2) Methods: Extracted premolars with similar root dimensions were assigned into two groups of 30 each for the metal and fiber posts. Teeth were mounted in acrylic blocks exposing 2 mm of the coronal root. Teeth were subjected to endodontic treatment and post-space preparations. Two groups were further subdivided into three sub-groups (n = 10) according to the size of the posts (# 4, 5 and 6). Posts were cemented with resin cement. Specimens were sectioned into 4 mm slices and subjected to the PBS test. (3) Results: The mean PBS was similar for the metal and fiber posts bonded with resin cement, showing a statistically significant result. An increase in post size increased the bond strength initially, but a further increase in size did not show any marked difference. A total of 71.66% of tested specimens failed with the adhesive failure mode. (4) Conclusions: Metal posts showed slightly higher retention compared to the fiber posts, although the p-value was similar for both types. An increase in the size of posts showed increased retention. The most common mode of failure was adhesive failure between cement and dentin.

The use of vaping or electronic cigarette devices (ECDs) has recently increased as an alternative to conventional tobacco smoking products. By recording the CIELAB coordinates (L*a*b*) and computing the total color difference (ΔE) values using a spectrophotometer, the effect of ECDs on contemporary aesthetic dental ceramics was investigated in this in-vitro study. A total of seventy-five (N = 75) specimens from five different (n = 15) dental ceramic materials (Pressable ceramics (PEmax); Pressed and layered ceramics (LEmax); Layered zirconia (LZr); Monolithic zirconia (MZr) and Porcelain fused to metal (PFM)) were prepared and exposed to aerosols produced by the ECDs. The color assessment was performed using a spectrophotometer at six time intervals (0 = baseline; 250-puff exposures; 500-puff exposures; 750-puff exposures; 1000-puff exposures; 1250-puff exposures; and 1500-puff exposures). By recording L*a*b* and computing total color difference (ΔE) values, the data were processed. A one-way ANOVA and Tukey procedure for pairwise comparisons were used to assess color differences between tested ceramics (p < 0.05). All test materials demonstrated significant color differences (ΔE) after exposure to vaping (p < 0.05). The LZr group displayed noticeably high ΔE values at all the distinct puff exposure intervals, with the highest ΔE value of (13.67) after 1500 puffs. The lowest (ΔE) values were observed in the PFM group after 250 and 500 puffs (0.85 and 0.97, respectively). With the exception of the group PEmax (p = 0.999), all groups produced readings of “ΔE” that indicated significant differences (p < 0.05) at various degrees of puff exposures. ECDs can noticeably alter the color of the dental ceramics affecting the esthetics of the patients. All the materials tested demonstrated significant color changes (ΔE > 3.33) above the clinically acceptable threshold, except for the PFM and PEmax group (ΔE < 3.33) which showed color stability after exposure to the ECDs.