When using the two-step putty-wash impression technique, pouring of the impressions may be postponed up to 30 hours; however, when using the one-step impression technique, pouring should be performed within 2 hours.

This assignment applies to all translations of the Work as well as to preliminary display/posting of the abstract of the accepted article in electronic form before publication. If any changes in authorship (order, deletions, or additions) occur after the manuscript is submitted, agreement by all authors for such changes must be on file with the Publisher. An author's name may be removed only at his/her written request. (Note: Material prepared by employees of the US government in the course of their official duties cannot be copyrighted.

The effect of dentin pretreatment with Desensitizing Paste containing 8% arginine and calcium carbonate on the retention of zirconium oxide (Y-TZP) crowns was tested. Forty molar teeth were mounted and prepared using a standardized protocol. Y-TZP crowns were produced using computer-aided design and computer-aided manufacturing (CAD-CAM) technology. The 40 prepared teeth were either pretreated with Desensitizing Paste or not pretreated. After two weeks, each group was subdivided into two groups, cemented with either Resin Modified Glass Ionomer Cement (RMGIC) or Self Adhesive Resin Cement (SARC)). Prior to cementation, the surface areas of the prepared teeth were measured. After aging, the cemented crown-tooth assemblies were tested for retentive strength using a universal testing machine. The debonded surfaces of the teeth and crowns were examined microscopically at 10× magnification. Pretreating the dentin surfaces with Desensitizing Paste prior to cementation did not affect the retention of the Y-TZP crowns. The retentive values for RMGIC (3.04 ± 0.77 MPa) were significantly higher than those for SARC (2.28 ± 0.58 MPa). The predominant failure modes for the RMGIC and SARC were adhesive cement-dentin and adhesive cement-crown, respectively. An 8.0% arginine and calcium carbonate in-office desensitizing paste can be safely used to reduce post-cementation sensitivity without reducing the retentive strength of Y-TZP crowns.

The dimensional stability of a thin intra sulcular impression material reproducing the preparation finish line was evaluated. Impressions were taken of a stainless-steel master model of a simulated abutment with a 'gingival sulcus' using Express regular, Express fast and Aquasil. The putty-wash two-step technique was applied with spacer thicknesses of 0.5, 1 and 1.5 mm. Mid mesiodistal and bucco-lingual measurements were taken directly from the sulcular impression material after 0.5, 2, 24, 48 and 72 h via a Toolmaker's microscope. The discrepancies between the measurements of the impression material and the master model were calculated. The discrepancies changed significantly over time (p<0.001). The use of a 0.5 mm spacer resulted in a negative deviation from the model (2-46 µm), minimally after 2 h. The use of 1 and 1.5 mm spacers showed a positive deviation from the model (21-52 µm) and both are equally recommended. Investment can be postponed until 72 h.