The scope of this work is to provide an overview of the influences of process parameters, print orientation, and post-process treatments of Ti6AlV4 processed by laser powder bed fusion on its microstructure and physical and mechanical properties and their anisotropic behavior. To avoid the influence of changes in powder quality and ensure comparability, experiments were carried out using a single batch of virgin powder. First, characterization of the density and surface roughness was performed to optimize the process parameters utilizing design of experiment. Tensile, notched bar impact and compression test specimens were built in three different orientations: vertically, horizontally, and inclined at 45° to the build plate. Later, the influence of the staircase effect and the possible course of anisotropy from vertical to horizontal were investigated. Subsequently, heat treatments for stress relief, furnace annealing, and hot isostatic pressing were performed. In addition to as-built samples, mechanical machining and a two-step electrochemical polishing surface treatment were applied to investigate the influence of the surface roughness. With parameter optimization, a relative density of 99.8% was achieved, and surface roughness was improved over default parameters, reducing Ra by up to 7 µm. Electrochemical polishing is a viable way to decrease the surface roughness. An Ra value of 1 µm and an Rz value of 4 µm can be achieved for 45° downskin surfaces with as-built surface roughness values of Ra 24 µm and Rz 117 µm. As-built and stress-relieved conditions show little anisotropy in their yield and tensile strength (max 2.7%), but there is a strong influence of the build orientation on necking, and brittle fracture behavior is shown due to the martensitic microstructure (up to 70%). Heat treatment can increase the ductility and further decrease the strength anisotropy with both furnace annealing and hot isostatic pressing delivering similar results for tensile properties, while angled samples exhibit behavior that is closer to vertical than horizontal, indicating a non-linear change in break behavior. Electrochemical polishing increases fracture necking, and its isotropy drastically increases from 4% to over 30% compared with as-built parts, which is close to the level of the machined specimen.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.