No abstract

No abstract

This research investigated the in-vitro wear and friction performance of polycarbonate urethane (PCU) 80A as they interact with articular cartilage, using a customised multidirectional pin-on-plate tester. Condyles were articulated against PCU 80A discs (Bionate I and Bionate II) (configuration 1) and the results arising from these tests were compared to those recorded during the sliding of PCU pins against cartilage plates (configuration 2). Configuration 1 produced steadily increasing coefficient of friction (COF) (up to 0.64 ± 0.05) and had the same trend as the cartilage-on-stainless steel articulation (positive control). When synovial fluid rather than bovine calf serum was used as lubricant, average COF significantly decreased from 0.50 ± 0.02-0.38 ± 0.06 for condyle-on-Bionate I (80AI) and from 0.41 ± 0.02-0.24 ± 0.04 for condyle-on-Bionate II (80AII) test configurations (p < 0.05). After 15 h testing, the cartilage-on-cartilage articulation (negative control) tests showed no cartilage degeneration. However, different levels of cartilage volume loss were found on the condyles from the positive control (12.5 ± 4.2 mm) and the PCUs (20.1 ± 3.6 mm for 80 AI and 19.0 ± 2.3 mm for 80AII) (p > 0.05). A good correlation (R =0.84) was found between the levels of average COF and the volume of cartilage lost during testing; increasing wear was found at higher levels of COF. Configuration 2 showed low and constant COF values (0.04 ± 0.01), which were closer to the negative control (0.03 ± 0.01) and significantly lower than configuration 1 (p < 0.05). The investigation showed that PCU is a good candidate for use in hemiarthroplasty components, where only one of the two articulating surfaces is replaced, as long as the synthetic material is implanted in a region where migrating cartilage contact is achieved. Bionate II showed better tribological performance, which suggests it is more favourable for use in hemiarthroplasty design.

Additive manufacturing offers exciting new possibilities for improving long‐term metallic implant fixation in bone through enabling open porous structures for bony ingrowth. The aim of this research was to investigate how the technology could also improve initial fixation, a precursor to successful long‐term fixation. A new barbed fixation mechanism, relying on flexible struts was proposed and manufactured as a push‐fit peg. The technology was optimized using a synthetic bone model and compared with conventional press‐fit peg controls tested over a range of interference fits. Optimum designs, achieving maximum pull‐out force, were subsequently tested in a cadaveric femoral condyle model. The barbed fixation surface provided more than double the pull‐out force for less than a third of the insertion force compared to the best performing conventional press‐fit peg (p < 0.001). Indeed, it provided screw‐strength pull out from a push‐fit device (1,124 ± 146 N). This step change in implant fixation potential offers new capabilities for low profile, minimally invasive implant design, while providing new options to simplify surgery, allowing for one‐piece push‐fit components with high levels of initial stability. © 2017 The Authors. Journal of Orthopaedic Research® Published by Wiley Periodicals, Inc. on behalf of the Orthopaedic Research Society. J Orthop Res 36:1508–1518, 2018.

No abstract