Tungsten and silicon carbide fibres have been coated with diamond using the HFCVD technique. The diamond volume fraction varied between 26% and 73%. Resonance in bending tests gave a Young's modulus of 880 GPa for the diamond coating. Tensile testing indicated that the diamond fracture strength was between 600 MPa and 2000 MPa, depending on the coating thickness, and thus the grain size, of the diamond. The strain to failure of the diamond coating in bending was approximately 0.15% for 25 μm thick films.