The microstructural alterations suffered during the process of drawing deformation and subsequent annealing of pearlitic steel wires, were evaluated by scanning electron microscopy and atomic force microscopy. The deformed material showed the curling structure in cross section while, in the longitudinal section, the lamellae was aligned with the drawing direction. The microstructural characterization of deformed samples also allowed observing an interlamellar spacing reduction and the intermediate lamellae alignment process. After the heat treatment at 1000ºC for 5 min the microstructure was restored, however, few recrystallized grains were observed. The recovery was the dominant phenomenon, due to factors associated with curling structure that inhibited recrystallization.

A pesquisa teve por objetivo descrever como a implementação de práticas da produção enxuta são benéficas no processo na produção de medicamentos manipulados, de modo a facilitar a entrega do produto para o cliente na hora certa, no tempo certo e com o pouco desperdício de recursos. De forma específica, apresentou-se o processo de manipulação de medicamentos encapsulados; elencou-se por meio da ferramenta dos sete desperdícios oportunidades de eliminação de desperdícios no processo e avaliou-se as práticas do programa 5S na farmácia. Este artigo fundamentou-se em uma pesquisa aplicada, com abordagem qualitativa e de caráter descritivo. Foram feitas análises sobre práticas de produção enxuta baseadas processo produtivo, fluxo de valor e meios de desperdícios. Foi definido o processo por meio da descrição de suas etapas e a elaboração de um fluxograma definindo sua cadeia de valor. Depois, foram avaliadas as práticas produtivas dos sete tipos de desperdícios e do programa 5S. O resultado permitiu verificar oportunidades de melhorias no processo de produção, trazendo benefícios, como o aumento da produtividade, a eliminação dos desperdícios durante o processo de produção, e a organização do ambiente de trabalho.

ResumoA combinação de propriedades apresentada pelos aços perlíticos permite sua aplicação em diversos segmentos. O objetivo deste trabalho foi caracterizar a microestrutura do aço SAE 1070 deformado via trefilação para a fabricação de fiomáquina. O aço foi trefilado a seco por 12 passes com reduções médias entre 15 e 21%. A caracterização microestrutural foi realizada com o auxílio da técnica de microscopia eletrônica de varredura e microscopia de força atômica. O material teve ainda seu comportamento mecânico avaliado por meio de ensaio de dureza Vickers e ensaio de tração. O material deformado apresentou a estrutura "curling" na seção transversal, enquanto que na seção longitudinal a maioria das lamelas se encontrava alinhadas com a direção de trefilação. Os ensaios de tração e dureza revelaram um aumento considerável da dureza e resistência do material após o processo de trefilação. Palavras-chave: SAE 1070; Trefilação; Caracterização microestrutural. MICROSTRUCTURAL CHARACTERIZATION AND MECHANICAL BEHAVIOR OF PEARLITIC STEEL WIRE DRAWING AbstractThe combination of properties of pearlitic steels allows its application in different segments. The objective of the present work was characterizing the microstructure of SAE 1070 steel wire drawing for manufacturing tire cords. The steel was dry drawn for 12 pass with average reductions between 15 to 21%. The microstructural characterization was performed with the aid of the scanning by electron microscopy and atomic force microscopy. The material mechanical behavior was also evaluated by Vickers hardness and tensile test. The deformed material showed a curling structure in cross section, while in longitudinal section, the majority of the lamellas was aligned with drawing direction. Tensile and hardness tests revealed a significant increase in hardness and strength of the material after the drawing process.

Compósitos poliméricos possuem uma crescente utilização com aplicação nos mais diversos setores. Por seu extenso ramo de aplicação, busca-se sempre a melhoria de seu desempenho por meio do reforço de sua matriz com fibras. Este trabalho teve como principal objetivo avaliar a viabilidade financeira da utilização da fibra de coco como reforço em compósitos com matriz de PVC para aplicação no ramo de construção civil. A pesquisa se caracteriza como quantitativa e bibliográfica. As informações de custos de matéria prima, mão de obra direta, custos indiretos de fabricação e produção mensal foram levantadas para determinar o custo unitário de produção e o preço de venda. O demonstrativo de resultado foi apresentado por meio do método de custeio por absorção, o seu valor presente líquido foi positivo, a taxa interna de retorno rentável e o seu payback aceitável. Por meio destes satisfatórios resultados, conclui-se que a utilização da fibra de coco como reforço em compósitos é viável financeiramente.

ResumoO objetivo deste trabalho foi analisar o refinamento da liga Al AA1070 deformada via ECAP (Equal Channel Angular Pressing) pela rota A em dois passes consecutivos. O material foi prensado a frio e a deformação verdadeira acumulada foi de 2,38. A caracterização microestrutural foi realizada com o auxílio da técnica de MEV. E a evolução da textura foi analisada através da técnica EBSD. A avaliação do comportamento mecânico da amostra foi realizada através do ensaio de microdureza de Vickers. Os resultados mostraram uma intensa redução no tamanho de grão após o 1º passe, seguido de um decréscimo considerável no 2º passe. A orientação encontrada na textura inicial evoluiu de {1 1 0} <7 7 10> para {5 13 1} <16 7 11> após o 2º passe. O comportamento mecânico apresentou um estado estacionário entre o 1º e 2º passe devido à ocorrência do fenômeno de recuperação dinâmica. Concluiu-se que um refinamento considerável foi obtido. Palavras-chave: ECAP; Alumínio; Microestrutura; Textura cristalográfica. Abstract The objective of this study was to analyze the refinement of AA1070 Al alloy deformed via ECAP by route A in two consecutive passes. The material was coldpressed and the true strain accumulated was 2.38. The microstructural characterization was performed with the aid of SEM technique. The evolution of texture was analyzed by EBSD technique. The evaluation of the mechanical behavior was performed using the Vickers hardness test. The results showed a marked decrease in grain size after the 1st pass, followed by a considerable decrease in the 2nd pass. The orientation found in the initial texture has evolved from {1 1 0} <7 7 10> to {5 13 1} <16 7 11> after the 2nd pass. The mechanical behavior showed a steady state between the 1st and 2nd pass due to the occurrence of the phenomenon of dynamic recovery. It was concluded that a considerable refinement was obtained