This study was conducted to enhance the tensile bond strengths of resin cements to zirconia ceramics. Fifty-six zirconia ceramic specimens (Cercon Base) and twenty-eight silica-based ceramic specimens (GN-1, GN-1 Ceramic Block) were air-abraded using alumina. Thereafter, the zirconia ceramic specimens were divided into two subgroups of 28 each according to the surface pretreatment; no pretreatment (Zr); and the internal coating technique (INT). For INT, the surface of zirconia was coated by fusing silica-based ceramics (Cercon Ceram Kiss). Ceramic surfaces were conditioned with/without a silane coupling agent followed by bonding with one of two resin cements; Panavia F 2.0 (PF) and Superbond C&B (SB). After 24 hours storage in water, the tensile bond strengths were tested (n=7). For both PF and SB, silanization significantly improved the bond strength to GN-1 and INT (p<0.05). The INT coating followed by silanizaton demonstrated enhancement of bonding to zirconia ceramics.

A resin coating should be required to improve dentin bonding performance of Panavia F in indirect restorations. However, direct composite restorations still provide higher bond strength compared to indirect restorations.

The purpose of this study was to evaluate coronal leakage inhibition using a resin-coating technique after endodontic treatment. Thirty-six human incisors were cut at the cementoenamel junction, and endodontic obturations were performed. The specimens were randomly divided into three groups according to post space preparation（10 mm depth） , resin coating, and temporization. For the resin coating, the dentin surface was coated with either a combination of Clearfil SE Bond and Protect Liner F（SE/PLF）or RZII（RZ） . Then, the specimens were stored in 37℃ distilled water for 24 hours and placed in 1％ methylene blue solution for 48 hours. After which, the specimens were sectioned faciolingually along the root canal and the length of dye penetration was measured from the cementoenamel junction. Three-way ANOVA revealed that the dye penetration scores were influenced by post space preparation, resin coating, and temporization. Resin coating with RZ significantly reduced the dye penetration score and SE/PLF completely eliminated dye penetration.