The FEL and PIC discs showed the lowest susceptibility to slow crack growth (SCG), whereas the LD and ZLS discs presented the highest. PIC presented the lowest elastic modulus and no crystals in its composition, while ZLS presented tetragonal zirconia. The overall strength and SCG of the new materials did not benefit from the additional phase or microconstituents present in them.
The aim of this study was to verify the effects of different surface treatments on the microtensile bond strength between resin cement and a hybrid ceramic. Thirty-two hybrid ceramic slices (8 × 10 × 3 mm) were produced and allocated among four groups according to the surface treatment: Cont = no treatment, HA = 10% hydrofluoric acid applied for 60 seconds, PA = 37% phosphoric acid applied for 60 seconds and CJ = air abrasion with silica particle coated alumina (Cojet Sand, 3M ESPE, 30 μm/2.8 bar). As a control group, eight blocks of feldspathic ceramic (8 × 10 × 3 mm) were etched by hydrofluoric acid for 60 seconds (VMII). After the surface treatments, the ceramic slices were silanized (except the Cont group) and adhesively cemented to composite resin blocks (8 × 10 × 3 mm ) with a load of 750 g (polymerized for 40 seconds each side). The cemented blocks were cut into beams (bonded surface area of ∼1 mm(2)). Half of the beams were aged (thermocycling of 5°C-55°C/6000 cycles + water storage at 37°C/60 days), and the other half were tested immediately after being cut. Data were analyzed by Kruskal-Wallis and Dunn tests (non-aged groups) and by one-way analysis of variance and Tukey test (aged groups; α=0.05%). The mode of failure was classified by stereomicroscopy. The surface treatment significantly affected the bond strength in each set of groups: non-aged (p=0.001) and aged (p=0.001). Before being aged, samples in the CJ, HA, and PA groups achieved the highest bond strength values. However, after being aged, only those in the HA group remained with the highest bond strength values. Adhesive failure was found most often. In conclusion, hydrofluoric acid etching should be used for surface conditioning of the studied hybrid ceramic.
This study investigated the flexural strength of eight fiber posts (one carbon fiber, one carbon/quartz fiber, one opaque quartz fiber, two translucent quartz fiber, and three glass fiber posts).
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.