The hydrothermal synthesis of aluminophosphate molecular sieve type AlPO4-11 was processed from chemicals containing psueudobohemite, 85% phosphoric acid, water, and di-isopropylamine as templating agent. The crystallization of the samples was studied by taking samples in times from 2 to 74 h. The obtained white powder products were characterized by X-ray diffraction patterns (XRD), Fourier transform infrared spectroscopy (FT-IR), thermogravimetry (TG) and differential scanning calorimetry (DTG) data and pH measurement of the mother liquor. The pore volume, as determined from TG and DTG curves, was ca. 0.17 cm3g−1. The percent relative crystallinity was determined by XRD and FT-IR methods. The crystallization kinetics evidenced that the hydrothermal synthesis of AlPO4-11 exhibited in its initial phase a behavior of first order reaction with a specific velocity constant of ca. 0.25 h−1, as determined from XRD and FT-IR data. The results obtained by both X-ray diffraction and infrared spectroscopy are comparable, and FT-IR is found to be a rapid method for estimating crystallinity and structure of aluminophosphate.

The hydrothermal synthesis of aluminophosphate molecular sieve type AlPO4-11 was processed from chemicals containing psueudobohemite, 85% phosphoric acid, water, and di-isopropylamine as templating agent. The crystallization of the samples was studied by taking samples in times from 2 to 74 hours. The obtained white powder products have been characterized by XRD patterns, FT-IR spectra, thermogravimetric data, scanning electron microscopy and pH measurement of the mother liquor. The pore volume, as determined from TG and DTG curves, was ca. 0.17 cm3g-1. The crystallization process of the aluminophosphate exhibited in its initial phase a behavior of first order reaction with a specific velocity constant of ca. 0.25 h-1, as determined from XRD and FT-IR data.