No abstract

No abstract

Films and edible coatings based on biopolymers have been developed as a packaging, which can be obtained from biodegradable materials and have properties similar to common plastics. These edible materials have many applications in the food industry, preventing mass transfer between the product and the surrounding environment. The objective of this study was to develop and evaluate the physicochemical and mechanical properties of edible films based on cassava starch (CS), whey protein (WP), and beeswax (BW). Response surface methodology has been used and the experiments were carried out based on face-centred composite design. On the other hand, three CS-based controls were formulated to evaluate the effect of the inclusion of WP and BW. The optimization of multiple responses established the optimal formulation: CS (3.17 %), WP (1.30 %), BW (0.50 %), presenting the following response variables: tensile stress (1.92 MPa), elongation (40.4 %), Young's modulus (42.1 MPa), water vapor permeability 1.79 × 10 −11 (g mm/s cm 2 Pa), swelling capacity (300.3 %), thickness (0.128 mm), moisture content (6.74 %), and colour: lightness (89.9), chromaticity a∗ (-1.8), chromaticity b∗ (7.7), saturation (9.9), tone (101.1°), and yellowness index (17.7). The selection and evaluation of this optimal formulation are essential because it is the material that shows the best possible mechanical and physicochemical properties using the studied components. The results, especially its good mechanical properties and low permeability to water vapour, would allow its application as a coating for fruits, vegetables, among others, effectively delaying its weight loss due to dehydration.

This work aims to improve the physicochemical properties of polylactic acid (PLA) and thermoplastic yam starch (TPS) blends using epoxidised sesame oil (ESO). We used epoxidised sesame oil from two Colombian Caribbean crops: Dioscorea rotundata and Sesamum indicum, with an oil substitution of 58.4 %. Films were obtained through extrusion and compression moulding processes. Moisture content, solubility, contact angle, and mechanical, barrier, and structural properties were determined using optical and scanning electron microscopy, infrared Fourier transform spectroscopy. Thermal analyses were also performed using thermogravimetry and differential scanning calorimetry techniques. The results suggest that the PLA and TPS interactions can be improved with the addition of ESO as coupling agent, enhancing the interfacial adhesion between the polymers, and favouring the smoothness of the film surface. Furthermore, the ESO addition led to increased thermal stability while restricting molecular mobility, indicating a coupling agent effect. In conclusion, the use of epoxidised oil for preparing films based on high PLA content and TPS allows obtaining enhanced interfacial adhesion. Considering the above, the developed materials have potential application in semi-rigid food packaging.

The blackberry is a fragile fruit with a high degree of decomposition, which limits its shelf life. The effect of an edible coating (EC) based on cassava starch, whey protein, beeswax, chitosan, glycerol, stearic acid, and glacial acetic acid on the shelf life of fruit stored at 4 C was evaluated. The physical, chemical, physical, microbiological, and sensorial quality was evaluated, comparing with a fresh control fruit. The EC had a positive effect on the physicochemical and sensorial properties (mainly in texture, flavor, and aromas), due to the reduction of physiological processes, whereas the color changes are mainly due to anthocyanin losses. After 10 days of storage, weight losses were 39.6% lower and firmness was 81.4% higher; while chitosan reduced the mold and yeast count. The EC increased the useful life of the Andean blackberries by 100%.