Adsorbent OxidationArsenite Removal a b s t r a c t Arsenite (As(III)) is more toxic and more difficult to remove from water than arsenate (As(V)).As there is no simple treatment for the efficient removal of As(III), an oxidation step is always necessary to achieve higher removal. However, this leads to a complicated operation and is not cost-effective. To overcome these disadvantage, a novel Fe-Mn binary oxide material which combined the oxidation property of manganese dioxide and the high adsorption features to As(V) of iron oxides, were developed from low cost materials using a simultaneous oxidation and coprecipitation method. The adsorbent was characterized by BET surface areas measurement, powder XRD, SEM, and XPS. The results showed that prepared Fe-Mn binary oxide with a high surface area ð265 m 2 g À1 Þ was amorphous. Iron and manganese existed mainly in the oxidation state þIII and IV, respectively. Laboratory experiments were carried out to investigate adsorption kinetics, adsorption capacity of the adsorbent and the effect of solution pH values on arsenic removal. Batch experimental results showed that the adsorbent could completely oxidize As(III) to As(V) and was effective for both As(V) and As(III) removal, particularly the As(III). The maximal adsorption capacities of As(V) and As(III) were 0:93 mmol g À1 and 1:77 mmol g À1 , respectively. The results compare favorably with those obtained using other adsorbent. The effects of anions such as SO 2À 4 , PO 3À 4 , SiO and humic acid (HA), which possibly exist in natural water, on As(III) removal were also investigated. The results indicated that phosphate was the greatest competitor with arsenic for adsorptive sites on the adsorbent. The presence of sulfate and HA had no significant effect on arsenic removal. The high uptake capability of the Fe-Mn binary oxide makes it potentially attractive adsorbent for the removal of As(III) from aqueous solution.

CuFe 2 O 4 /activated carbon magnetic adsorbents, which combined the adsorption features of activated carbon with the magnetic and the excellent catalytic properties of powdered CuFe 2 O 4 , were developed using a simple chemical coprecipitation procedure. The prepared magnetic composites can be used to adsorb acid orange II (AO7) in water and subsequently, easily be separated from the medium by a magnetic technique. CuFe 2 O 4 /activated carbon magnetic adsorbents with mass ratio of 1:1, 1:1.5 and 1:2 were prepared. Magnetization measurements, BET surface area measurements, powder XRD and SEM were used to characterize the prepared adsorbents. The results indicate that the magnetic phase present is spinel copper ferrite and the presence of CuFe 2 O 4 did not significantly affect the surface area and pore structure of the activated carbon. The adsorption kinetics and adsorption isotherm of acid orange II (AO7) onto the composites at pH 5.2 also showed that the presence of CuFe 2 O 4 did not affect the adsorption capacity of the activated carbon. The thermal decomposition of AO7 adsorbed on the activated carbon and the composite was investigated by in situ FTIR, respectively. The results suggest that the composite has much higher catalytic activity than that of activated carbon, attributed to the presence of CuFe 2 O 4 . The variation of the adsorption capacity of the composites after several adsorption-regeneration cycles has also been studied.

No abstract