The effects of different process parameters on the microstructure and mechanical properties of Zr-based bulk metallic glass were studied by using four factors and four levels of orthogonal experiment. Through the observation and analysis of the X-ray diffraction pattern, room temperature compressibility, microhardness distribution and transmission electron micrograph of the [Zr0.72-x(Cu0.59Ni0.41)0.28+x]88-yAl12+y (atomic percent) amorphous alloy with different process parameters, the results show that the compressive strength of the amorphous alloys with composition of [Zr0.73(Cu0.59Ni0.41)0.27]88Al12 and [Zr0.73(Cu0.59Ni0.41)0.27]87Al13 amorphous alloy under the corresponding processing parameters has reached 2411MPa and 1993MPa, and the plastic strain of the alloys is 33.8% and 19.3%. At the same time, through orthogonal analysis, in the four process parameters, the superheat temperature of the melt during the preparation of the alloy mainly affects the compressive strength of the alloy, while the cooling rate of the melt during the preparation of the alloy has a great influence on the plastic properties of the alloy.

China is a large agricultural country, but the water resource amount can not meet the demand of irrigation, Through setting up the long-range monitoring system of irrigated area water that is operated very good, can improve the utilization efficiency of irrigating water resources, to economize irrigate water consumption greatly. This paper introduces MultiAgent theories in the long-range monitoring system of irrigated area, has set up a kind of long-range monitoring system of irrigated area based on Multi-Agent, this system is formed by control center Multi-Agent subsystems, the communication layer that is formed by communication Agent and GSM communication network, and some monitoring station MultiAgent subsystems. The control center Multi-Agent subsystems and monitoring station Multi-Agent subsystems realize the longrange control of the irrigated area through the information transmission of communication layer. Through emulation test, the system run well.

Zirconium base metallic glasses [Zr0.73(Cu0.59Ni0.41)0.27]87Al13 was fabricated by industrial zirconium with low purity and high purity zirconium according to different quality ratios in order to study the effect of raw material purity on the structure and properties of metallic glasses. The results showed that the complete metallic glasses was failed to be fabricate with low purity zirconium. And the compression process was typical brittle fracture with low compressive strength and without plastic strain. The glasses forming ability of low purity zirconium metallic glass with different purity was significantly improved after the addition of yttrium element. The compression experiments showed that the compressive strength and plasticity of metallic glasses were improved, and the microhardness was also increased. It indicates that yttrium element can eliminate the adverse effect of impurity in low purity zirconium on the glasses forming ability of the alloy and improve the structural properties of the metallic glasses.

No abstract