Fiber reinforced thermoplastics (FRTP), reinforced with glass or carbon fibers, are used to improve the mechanical strength of injection-molded products. However, FRTP has problems such as the formation of weld lines, the deterioration of appearance due to the exposure of fibers on the molded product surface, and the deterioration of the strength of molded products due to the fiber orientation in the molded products. We have designed and fabricated an injection mold capable of melt flow control and induction heating and cooling. This mold can both heat and cool the injection mold. It can also control the melt flow direction using a movable core pin. In this study, the above-mentioned mold was used for the molding of carbon fiber reinforced semi-aromatic polyamide. As a result, we found that increasing the heating temperature of the mold and increasing melt flow control volume contribute to the prevention of the generation of a weld line and the exposure of fibers on the molded product surface, as well as to the formation of a flat surface and increased bending strength. The relationships of these results with the carbon fiber orientation in the molded products and the crystallization of semi-aromatic polyamide were also examined in this study.

Fiber reinforced thermoplastics (FRTP), which is reinforced with glass or carbon fibers, are used to improve the mechanical strength of injection-molded products. However, FRTP has problems such as the formation of weld lines, the deterioration of the appearance due to the exposure of fibers on the molded product surface, and the deterioration of the strength of molded products due to the fiber orientation in the molded products. We have designed and fabricated an injection mold capable of melt flow control and induction heating and cooling that has the functions of both heating and cooling the injection mold as well as the function of controlling the melt flow direction using a movable core pin. In this study, the above-mentioned mold was used for the molding of carbon fiber reinforced semi-aromatic polyamide. As a result, we found that increasing the heating temperature of the mold and increasing melt flow control volume contribute to the prevention of the generation of a weld line and the exposure of fibers on the molded product surface, as well as to the formation of a flat surface and increased bending strength. The relationships of these results with the carbon fiber orientation in the molded products and the crystallization of semi-aromatic polyamide were also examined in this study.