Abstract-ZnO nano-rods grown by gaseous-disperse synthesis (GDS) are confirmed by XRD analysis to have the wurtzite crystal structure. The obtained crystallites, as found from SEM studies, are 57±9 nm in diameter and 470±30 nm long on the average. Two emission bands of photoluminescence from ZnO nano-rods observed at room temperature are centered at 376 nm and 520 nm. A bio-sensitive layer is prepared by immobilization of Anti-Salmonella antibodies (Ab) from liquid solutions on the ZnO surface. Immobilization of the bio-sensitive layer onto ZnO nano-rods is found to increase the intensity of PL. After further reaction with Salmonella antigens (Ag) the PL intensity is found to decrease proportional to antigen concentrations in the range of 1000 -1000000 cell/ml. The possible mechanism of biosensor response is suggested and discussed.

No abstract

Анотація. Досліджено вплив наявності у довкіллі аміаку або парів хлористого водню на фотолюмінесцентні властивості ансамблю наночастинок барвників на базі комплексів 4-валентного стануму. Виявлено, що чутливими до аміаку є барвники, що містять аміновий замісник бензоїльного типу у гідразонному фраґменті, а до хлористого водню-барвники із гідроксильним замісником. Обидві групи сполук суттєво зменшують інтенсивність свого світіння при наявності у І. К. Дойчо, С. А. Гевелюк, Я. І. Лепіх, Е. Ришякевич-Пасек 32 довкіллі відповідного газу. Послаблення світіння є досить стійким і поновлення люмінесцентних властивостей зразка можливе лише внаслідок низькотемпературного відпалу. Ключові слова: барвники, фотолюмінесценція, аміак, хлористий водень, давачі газу, екологія FEATURES OF GAS-SENSIBILITY OF DYES ON THE BASE OF 4-VALENCE STANNUM COMPLEXES

No abstract

No abstract