The thermoelectric properties of polycrystalline samples of GeTe-rich side solid solutions (GeTe)l -, .. (AgSbTe,), for the compositions z = 0.00, 0.10, 0.15, 0.20, and 0.29 are investigated. The temperature dependences of the Seebeck coefficient and the electrical resistivity and the dependences of the total thermal conductivity a t 300 K versus composition are measured. The temperature dependences of the total thermal conductivity and the thermoelectric figure of merit 2 are calculated. The composition with maximum value of 2 is determined as GeTe + 20 mol% AgSbTe,.The reasons for the maximum thermoelectric figure of merit for this composition and for the anomaly changes in the thermoelectric parameters and the sharp increase of 2 in the region of phase transitions (Oi-C&,)are discussed.Die thermoelektrischen Eigenschaften von polykristallinen Proben der Mischkristalle (GeTe)l -, * . (AgSbTe,), nahe der Verbindung GeTe mit den Zusammensetzungen z = 0,OO; 0,lO; 0,15; 0,20 und 0,29 werden untersucht. Die Temperaturabhangigkeiten der Thermospannung und des spezifischen elektrischen Widerstandes und die Abhiingigkeiten der thermischen Leitfiihigkeit bei 300 K von der Zusammensetzung werden gemessen. Die Temperaturabhingigkeiten der thermischen Leitfiihigkeit und des thermischen Wirkungsgrades 2 werden berechnet. Die Zusammensetzung mit dem Maximalwert von 2 wird bestimmt zu GeTe + 20 Molyo AgSbTe,. Die Ursachen fur den maximalen Wirkungsgrad bei dieser Zusammensetzung und fur das scharfe Anwachsen von 2 im Gebiet der Phesenumwandlung (Oi-Civ) fur alle Zusammensetzungen werden diskutiert.