Cobalt ferrite nanoparticle (CFN) has received attention in magnetic resonance imaging (MRI) as a promising contrast agent due to its higher saturation magnetization and magneto-crystalline anisotropy. However, the in vitro cytotoxicity of CFN has raised concern for its biomedical application as a diagnostic agent. The coating of CFN by a biocompatible polymer such as chitosan (CH) might lessen the biocompatibility concern. Therefore, in this study, we examined the applicability of chitosan-coated cobalt ferrite nanoparticle (CCN) as an MRI contrast dye and investigated its biocompatibility in vivo. Phantom MRI images revealed that the relaxivity of CCN was 121 (±8) mM–1s–1, indicating the potential of CCN as a T 2-weighted contrast agent. A single intravenous (iv) administration of CCN (10 mg/kg) improved the contrast of magnetic-resonance-imaging-based angiography (MRA) and brain-MRI in male albino Wistar rats compared to the control. Furthermore, toxicity studies dependent on dose (1–20 mg/kg) and time (1–28 days) in male albino Wistar rats confirmed the in vivo biocompatibility of CCN. The physical, hematological, biochemical, and histopathological observation assured that a single iv injection of CCN up to 20 mg/kg was well adjusted with liver, kidney, heart, and brain functions. The findings of the current study consolidate CCN as a promising candidate for MRI contrast dye.

Biomedical applications of ZnFe2O4 nanoparticle are preferable among all kinds of ferrites due to the compatibility of Zn2+ ions for human bodies. We have followed the soft chemical route to synthesize chitosan and PEG coated ZnFe2O4 nanoparticles and also the chitosan-coated-nanoparticles encapsulated with liposome. X-ray diffraction studies by the Mo Kα target, showed the formation of single phase spinel structure. The lattice parameter turned out to be 8.48Å and grain size ~ 4.8 nm (± 0.1 nm). Similar particle size was observed by transmission electron microscope analysis. HRTEM studies showed the distinct lattice fringes thus confirming the good crystallinity of the synthesized nanoparticles. M-H curve at room temperature showed the prepared sample was superparamagnetic in nature, which is also confirmed by the doublets of Mössbauer spectroscopy. Relaxivity values (r2) of Chitosan and PEG coated ZnFe2O4 nanoparticles are 68 and 76 mM−1s−1 respectively. In order to achieve further biocompatibility the chitosan-coated-nanoparticles were encapsulated with liposome. The r2 relaxivity was found as 54mM−1s−1. MR images obtained from the in vitro experiments based on phantoms demonstrated good contrast enhancement. Induction heating of bare and coated particles was investigated to reveal the self heating temperature rising properties of ZnFe2O4 nanoparticles.

We synthesized manganese ferrite (MnFe2O4) nanoparticles of different sizes by varying pH during chemical co-precipitation procedure and modified their surfaces with polysaccharide chitosan (CS) to investigate characteristics of hyperthermia and magnetic resonance imaging (MRI). Structural features were analyzed by X-ray diffraction (XRD), high-resolution transmission electron microscopy (TEM), selected area diffraction (SAED) patterns, and Mössbauer spectroscopy to confirm the formation of superparamagnetic MnFe2O4 nanoparticles with a size range of 5–15 nm for pH of 9–12. The hydrodynamic sizes of nanoparticles were less than 250 nm with a polydispersity index of 0.3, whereas the zeta potentials were higher than 30 mV to ensure electrostatic repulsion for stable colloidal suspension. MRI properties at 7T demonstrated that transverse relaxation (T2) doubled as the size of CS-coated MnFe2O4 nanoparticles tripled in vitro. However, longitudinal relaxation (T1) was strongest for the smallest CS-coated MnFe2O4 nanoparticles, as revealed by in vivo positive contrast MRI angiography. Cytotoxicity assay on HeLa cells showed CS-coated MnFe2O4 nanoparticles is viable regardless of ambient pH, whereas hyperthermia studies revealed that both the maximum temperature and specific loss power obtained by alternating magnetic field exposure depended on nanoparticle size and concentration. Overall, these results reveal the exciting potential of CS-coated MnFe2O4 nanoparticles in MRI and hyperthermia studies for biomedical research.

No abstract

No abstract