This research discussed the influenced of different preparation methods of Carrageenan fillers as new natural biodegradable additives in Natural Rubber (NR) latex compound. NR latex compounds with addition of 2 phr Carrageenan fillers was prepared through normal pre-vulcanization method which the NR latex compound was subjected to 70 o C denoted as Method 1. The preparation of NR latex compounds with 2 phr Carrageenan fillers without temperature is denoted as Method 2. The unfilled NR Latex films also was prepared as a control through Method 1. The crosslink density and mechanical properties of NR Latex films were investigated via swelling test and mechanical testing (tensile and tear) respectively. The swelling test results shows that Method 2 have highest crosslink density where the crosslink density and mechanical properties via Method 1 shows a decreased value. This may contribute from the hydration of carrageenan at temperature of 40 o C-70 o C. The experimental results indicate that the addition of carrageenan with elimination of pre-vulcanization step is mainly responsible for the enhancement of crosslink density and mechanical properties compared to Method 1. Method 2 gives higher crosslink density, tear strength and lower modulus as evaluated from the mechanical properties. Carrageenan can be added as natural filler in NR Latex films with gives better interaction between rubber matrix and fillers with softer NR latex films which required in NR latex products especially gloves.

No abstract

No abstract