Faujasite (FAU) Y zeolite assemblies with high mesoporosity (Sext. = 347 m2 g−1 and Vmeso = 0.52 cm3 g−1) were synthesised using sustainable and economic cellulose nanocrystals (CNCs) via a...

Mesostructured zeolitic materials (MZMs) with relatively high acidity in comparison with the mesoporous siliceous MCM-41 were prepared via an efficient, mild, and simple post-synthetic treatment of Y zeolite facilitated by microwave irradiation, i.e., microwave-assisted chelation (MWAC). The disordered mesoporous aluminosilicates materials (DMASs) of MZM were created from Y zeolite in the absence of using mesoscale templates. The prepared DMASs showed the good mesoporous features with the mesopore area and volume of ∼260 m 2 g −1 and ∼0.37 cm 3 g −1 , respectively, and with the mesopore sizes distributed in a range of 2-10 nm. MZMs possess a total acidity of about 0.6 mmol g −1 and exhibited comparatively superior catalytic activity to the parent Y zeolite and MCM-41 in the vapor phase catalytic dealkylation of 1,3,5-triisopropylbenzene (TiPBz) and liquid phase catalytic aldol condensation of benzaldehyde with 1-heptanal. Although the yield loss was inevitable for preparing MZMs using the MWAC method, the preliminary economic analysis of the preparation cost of MZMs showed the promise. Additionally, a comprehensive comparison of the state-of-the-art mesoporous materials concerning their sustainable aspects was made, showing that MZMs are promising mesoporous materials for further development and functionalization for catalysis.

Thi s v e r sio n is b ei n g m a d e a v ail a bl e in a c c o r d a n c e wit h p u blis h e r p olici e s.S e e h t t p://o r c a . cf. a c. u k/ p olici e s. h t ml fo r u s a g e p olici e s. Co py ri g h t a n d m o r al ri g h t s fo r p u blic a tio n s m a d e a v ail a bl e in ORCA a r e r e t ai n e d by t h e c o py ri g h t h ol d e r s .

No abstract