Crystalline solids with extended non-interpenetrating three-dimensional crystal structures were synthesized that support well-defined pores with internal diameters of up to 48 angstroms. The Zn4O(CO2)6 unit was joined with either one or two kinds of organic link, 4,4',4''-[benzene-1,3,5-triyl-tris(ethyne-2,1-diyl)]tribenzoate (BTE), 4,4',44''-[benzene-1,3,5-triyl-tris(benzene-4,1-diyl)]tribenzoate (BBC), 4,4',44''-benzene-1,3,5-triyl-tribenzoate (BTB)/2,6-naphthalenedicarboxylate (NDC), and BTE/biphenyl-4,4'-dicarboxylate (BPDC), to give four metal-organic frameworks (MOFs), MOF-180, -200, -205, and -210, respectively. Members of this series of MOFs show exceptional porosities and gas (hydrogen, methane, and carbon dioxide) uptake capacities. For example, MOF-210 has Brunauer-Emmett-Teller and Langmuir surface areas of 6240 and 10,400 square meters per gram, respectively, and a total carbon dioxide storage capacity of 2870 milligrams per gram. The volume-specific internal surface area of MOF-210 (2060 square meters per cubic centimeter) is equivalent to the outer surface of nanoparticles (3-nanometer cubes) and near the ultimate adsorption limit for solid materials.

Supersized pores: A new mesoporous metal–organic framework that is mainly composed of Tb3+ ions and tripodal carboxylate ligands has cages of 3.9 and 4.7 nm in diameter (see picture). The evacuated framework is robust and can accommodate gases or ferrocene molecules, as verified by gas‐sorption measurements and luminescence studies.

No abstract

No abstract

Among recently synthesized isoreticular metal-organic frameworks (IRMOFs), interpenetrating IRMOFs show high hydrogen adsorption capacities at low temperature and under ambient pressure. However, little is known about the molecular basis of their hydrogen binding properties. In this work, we performed grand canonical Monte Carlo (GCMC) simulations to investigate the effect of catenation on the interactions between hydrogen molecules and IRMOFs. We identified the adsorption sites and analyzed the adsorption energy distributions. The simulation results show that the small pores generated by catenation can play a role to confine the hydrogen molecules more densely, so that the capacity of the interpenetrating IRMOFs could be higher than that of the non-interpenetrating IRMOFs.