The influence of processing parameters (slab thickness, water flow of interstand cooling and oil flow in roll gap lubrication system) on the thickness and composition of the tertiary scale formed during hot strip rolling, was studied in a low carbon steel in factory. The scale formed on the rolled surface was characterized by scanning electron microscopy and Mössbauer spectroscopy. It was observed that the combined effect of a greater rolling oil volume applied, larger bar thickness, and smaller amount of water flow during interstand cooling reduces the tertiary scale thickness. Besides, a smaller crack density in the samples is associated with greater rolling oil volume and smaller oxide scale thickness. The principal phase of the scale formed in hot-rolled steel strips is stoichiometric magnetite, without isomorphic substitutions.

No abstract

A telescopicidade é um defeito de forma de bobina caracterizada pelo deslocamento transversal ao sentido de laminação/bobinamento, de uma ou mais espiras, que pode ser causada por uma série de variáveis do processo de produção de tiras a quente. Cada cliente-seja ele interno ou externo-tem uma tolerância de aceite para a medida desta telescopicidade em seu pedido. Caso o valor ultrapasse esse limite, a bobina necessita ser reprocessada em linhas posteriores ao LTQ, como por exemplo, um laminador de acabamento ou linha de tesouras, antes de ser despachada para o cliente final. Com o objetivo de reduzir o retrabalho de bobinas-processo este que somente agrega custo ao produto-foi desenvolvido e implantado no LTQ da ArcelorMittal Tubarão um dispositivo de correção de telescopicidade. Este trabalho tem por finalidade apresentar os resultados atingidos após a implantação desta inovação tecnológica.