We fabricated a biomimetic nanofiltration (NF) membrane by immobilizing an Aquaporin Z (AqpZ)-incorporated supported lipid bilayer (SLB) on a layer-by-layer (LbL) complex polyelectrolyte membrane to achieve excellent permeability and salt rejection with a high stability. The polyelectrolyte membranes were prepared by LbL assembly of poly(ethylenimine) (PEI) with positive charges and poly(sodium 4-styrenesulfonate) (PSS) with negative charges alternately on a porous hydrolyzed polyacrylonitrile (H-PAN) substrate. AqpZ-incorporated 1,2-dioleloyl-sn-glycero-3-phosphocholine (DOPC)/1,2-dioleoyl-3-trimethylammo-nium-propane (chloride salt) (DOTAP) vesicles with positive charges were deposited on the H-PAN/PEI/PSS polyelectrolytes membrane surface. The resulting biomimetic membrane exhibited a high flux of 22 L·m(-2)·h(-1) (LMH), excellent MgCl2 rejection of ∼97% and NaCl rejection of ∼75% under an operation pressure of 0.4 MPa. Due to the attractive electrostatic interaction between SLB and the polyelectrolyte membrane, the biomimetic membrane showed satisfactory stability and durability as well as stable NF flux and rejection for at least 36 h. In addition, the AqpZ-containing biomimetic membrane was immersed in a 0.24 mM (critical micellar concentration, CMC) Triton X-100 solution for 5 min. The flux and rejection were slightly influenced by the Triton X-100 treatment. The current investigation demonstrated that the AqpZ-incorporated biomimetic membranes fabricated by the LbL method led to excellent separation performances and robust structures that withstand a high operation pressure for a relatively long time.

No abstract

No abstract

We demonstrated a novel AquaporinZ (AqpZ)-incorporated double-skinned forward osmosis (FO) membrane by layer-by-layer (LbL) assembly strategy. Positively charged poly(ethyleneimine) (PEI) and negatively charged poly(sodium 4-styrenesulfonate) (PSS) were alternately deposited on both the top and bottom surfaces of a hydrolyzed polyacrylonitrile (H-PAN) substrate. Subsequently, an AqpZ-embedded 1,2-dioleloyl-sn-glycero-3-phosphocholine (DOPC)/1,2-dioleoyl-3-trimethylammonium- propane (chloride salt) (DOTAP) supported lipid bilayer (SLB) was formed on PSS-terminated (T-PSS) membrane via vesicle rupture method. The morphology and structure of the biomimetic membranes were characterized by in situ atomic force microscopy (AFM), scanning electron microscope (SEM), Fourier transform infrared spectrometer using the attenuated total reflection technique (ATR-FTIR), and contact angle. Moreover, the FO performance of the resultant membrane was measured by using 2 M MgCl2 solution as draw solution and deionized (DI) water as feed solution, respectively. The membrane with a protein-to-lipid weight ratio (P/L) of 1/50 exhibits 13.2 L/m2h water flux and 3.2 g/m2h reversed flux by using FO mode, as well as 15.6 L/m2h water flux and 3.4 L/m2h reversed flux for PRO mode (the draw solution is placed against the active layer). It was also shown that the SLB layer of the double-skinned FO membrane can increase the surface hydrophilicity and reduce the surface roughness, which leads to an improved anti-fouling performance against humic acid foulant. The current work introduced a new method of fabricating high performance biomimetic FO membrane by combining AqpZ and a double-skinned structure based on LbL assembly.

No abstract