This work investigated polyethyleneimine (PEI)-introduced chitosan (CS) (CS/PEI) nanoparticles as non-viral carrier of plasmid DNA for rat mesenchymal stem cells (MSCs). The CS/PEI nanoparticles were prepared by the emulsifier-free emulsion polymerization of methyl methacrylate monomer induced by a small amount of t-butyl hydroperxide in the presence of different concentrations of PEI mixed with CS. The resulting nanoparticles were characterized by their surface properties and buffering capacity. In vitro gene transfection was also evaluated. The introduction of PEI affected the surface charge, dispersing stability and buffering capacity of the nanoparticles. The CS/PEI nanoparticles formed a complex upon mixing with a plasmid DNA of luciferase. The complex enhanced the level of gene transfection and prolonged the time period of expression for MSCs, compared with those of plasmid DNA-original CS and PEI nanoparticles. Cytotoxicity of CS/PEI complexes with plasmid DNA was significantly low, depending on the amount of PEI introduced. It is concluded that the CS/PEI nanoparticle was a promising carrier for gene delivery of MSCs.

No abstract

This work aims to enhance the polarity of natural rubber by grafting copolymers onto deproteinized natural rubber (DPNR) to improve its compatibility with silica. Poly(acrylic acid-co-acrylamide)-grafted DPNR ((PAA-co-PAM)-DPNR) was successfully prepared by graft copolymerization with acrylic acid and acrylamide in the latex stage, as confirmed by FTIR. The optimum conditions to obtain the highest conversion, grafting efficiency, and grafting percentage were a reaction time of 360 min, a reaction temperature of 50 °C, and an initiator concentration of 1.0 phr. The monomer conversion, grafting efficiency, and grafting percentage were 91.9–94.1, 20.8–38.9, and 2.1–9.9%, respectively, depending on the monomer content. It was shown that the polarity of the natural rubber increased after grafting. The (PAA-co-PAM)-DPNR was then mixed with silica to prepare DPNR/silica composites. The presence of the (PAA-co-PAM)-DPNR and silica in the composites was found to improve the mechanical properties of the DPNR. The incorporation of 10 phr of silica into the (PAA-co-PAM)-DPNR with 10 phr monomer increased its tensile strength by 1.55 times when compared to 10 phr of silica loaded into the DPNR. The silica-filled (PAA-co-PAM)-DPNR provided s higher storage modulus, higher Tg, and a lower tan δ peak, indicating stronger modified DPNR/silica interactions and greater thermal stability when compared to silica-filled DPNR.