The dimensional stability and some mechanical properties were tested in plywood produced with veneers modified with 1.3-dimethylol-4.5-dihydroxyethyleneurea (DMDHEU). The experimental design included Betula sp. and Fagus sylvatica impregnated with 0.8 M, 1.3 M, and 2.3 M DMDHEU. The plywood consisted of five veneers glued with a phenolic resin. Dimensional stability tests were conducted after 10 cycles of soaking/oven-drying to determine volume changes and anti swelling efficiency (ASE). The mechanical properties tested were hardness (Brinell), modulus of elasticity in bending (MOE), bending strength (BS) and work to maximum load in bending (WMLB). The modified samples for both species were considerably more dimensionally stable than the untreated samples. The samples of Betula sp. and F. sylvatica modified with DMDHEU presented a MOE and a BS unaffected by the treatment. The WMLB was consistently lower in the modified samples than in the unmodified samples. As determined by the Brinell method, the DMDHEU-modified plywood of the Betula sp. and F. sylvatica was harder than the unmodified plywood.
Maintenance procedures of different wood coating systems were studied in field exposure trials with coated balcony constructions. Maintenance coatings were applied on one half of each of the balcony parts after 18 months and assessed after 24 months of total exposure time. It was found that the opaque white coating systems were the most durable ones reaching long intervals of required maintenance. For systems with lower durability on the maintained surfaces further degradation of the coatings was prevented. Different characteristics were observed for film forming and non film forming semi-transparent varnishes. Definitions of a series of limit states for coating systems on wood were suggested including esthetical limits and three levels of durability limits. Film forming coatings can reach two durability limits, i.e. the maintenance interval and the renovation interval. For non film forming coatings there is only one limit state of coating durability where maintenance is needed. The third durability limit is related to the coated substrate, i.e. the wood component, by the onset of decay in wood.
Wartungsmaßnahmen und Definition von Grenzzuständen für HolzaußenbeschichtungenZusammenfassung Wartungsmaßnahmen von verschiedenen Beschichtungssystemen für Holz wurden in Freilandbe-G. Grüll ( ) · M. Truskaller
Wood moisture content of coated panels of Scots pine sapwood was recorded during 18 months natural weathering in Vienna by logging electric resistance and temperature near the surface. Eight coating systems with various film thicknesses were used, including three solvent borne alkyd stains, three water borne acrylic stains and two water borne acrylic paints. At five sites in Europe wood moisture content of panels coated with three solvent borne alkyd stains, a brow acrylic stain and a white opaque acrylic paint was recorded weekly by changes in panel mass. Fluctuations in wood moisture content were influenced by the film thickness, moisture protection and colour of the coating systems used. Degradation phenomena led to decreasing moisture protection of less durable coating systems over time of exposure. Differences between the exposure sites were relatively low, except the site in the UK where moisture conditions were higher.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.