Giant dielectric permittivity was observed in La-modified PbTiO (3) (PLT) with A-site vacancy. The observed values of PLT with A-site vacancy are 1 order of magnitude larger than those of relaxor ferroelectrics. The giant relative dielectric permittivity, coupled with a low dielectric loss (tandelta approximately 0.03) of the PLT, potentially makes it one of the most promising materials for numerous modern technological applications.

The purpose of this paper is to investigate polarization characteristics of heat-treated Ni-based self-flux alloy coating in alkaline solution. Ni-based self-flux alloy powder was sprayed to a steel substrate using flame spray process, and heat treatments were performed in a vacuum furnace at 800℃, 900℃, 1000℃ and 1100℃. After heat treatments, corrosion tests were carried out using potentiostat/galvanostat at solution with pH 8 and pH 13. Corrosion potential(Ecorr) and corrosion current density(Icorr) could be analyzed from polarization curve. Anticorrosive effect of heat-treated coating at solution with pH 8 was relatively greater than at solution with pH 13. Heat-treated coating at 1100℃ showed the greatest anti-corrosion characteristics in alkaline solution.