Atomically thin tungsten disulfide (WS2), a structural analogue to MoS2, has attracted great interest due to its indirect-to-direct band-gap tunability, giant spin splitting, and valley-related physics. However, the batch production of layered WS2 is underdeveloped (as compared with that of MoS2) for exploring these fundamental issues and developing its applications. Here, using a low-pressure chemical vapor deposition method, we demonstrate that high-crystalline mono- and few-layer WS2 flakes and even complete layers can be synthesized on sapphire with the domain size exceeding 50 × 50 μm(2). Intriguingly, we show that, with adding minor H2 carrier gas, the shape of monolayer WS2 flakes can be tailored from jagged to straight edge triangles and still single crystalline. Meanwhile, some intersecting triangle shape flakes are concomitantly evolved from more than one nucleus to show a polycrystalline nature. It is interesting to see that, only through a mild sample oxidation process, the grain boundaries are easily recognizable by scanning electron microscopy due to its altered contrasts. Hereby, controlling the initial nucleation state is crucial for synthesizing large-scale single-crystalline flakes. We believe that this work would benefit the controlled growth of high-quality transition metal dichalcogenide, as well as in their future applications in nanoelectronics, optoelectronics, and solar energy conversions.

Molybdenum disulfide (MoS2) is back in the spotlight because of the indirect-to-direct bandgap tunability and valley related physics emerging in the monolayer regime. However, rigorous control of the monolayer thickness is still a huge challenge for commonly utilized physical exfoliation and chemical synthesis methods. Herein, we have successfully grown predominantly monolayer MoS2 on an inert and nearly lattice-matching mica substrate by using a low-pressure chemical vapor deposition method. The growth is proposed to be mediated by an epitaxial mechanism, and the epitaxial monolayer MoS2 is intrinsically strained on mica due to a small adlayer-substrate lattice mismatch (~2.7%). Photoluminescence (PL) measurements indicate strong single-exciton emission in as-grown MoS2 and room-temperature PL helicity (circular polarization ~0.35) on transferred samples, providing straightforward proof of the high quality of the prepared monolayer crystals. The homogeneously strained high-quality monolayer MoS2 prepared in this study could competitively be exploited for a variety of future applications.

Stable cycling of lithium metal anode is challenging due to the dendritic lithium formation and high chemical reactivity of lithium with electrolyte and nearly all the materials. Here, we demonstrate a promising novel electrode design by growing two-dimensional (2D) atomic crystal layers including hexagonal boron nitride (h-BN) and graphene directly on Cu metal current collectors. Lithium ions were able to penetrate through the point and line defects of the 2D layers during the electrochemical deposition, leading to sandwiched lithium metal between ultrathin 2D layers and Cu. The 2D layers afford an excellent interfacial protection of Li metal due to their remarkable chemical stability as well as mechanical strength and flexibility, resulting from the strong intralayer bonds and ultrathin thickness. Smooth Li metal deposition without dendritic and mossy Li formation was realized. We showed stable cycling over 50 cycles with Coulombic efficiency ∼97% in organic carbonate electrolyte with current density and areal capacity up to the practical value of 2.0 mA/cm(2)and 5.0 mAh/cm(2), respectively, which is a significant improvement over the unprotected electrodes in the same electrolyte.