Two crystalline polyimide nanofibers (PINFs) with different morphologies were prepared. The crystalline unit cells of the aromatic PI crystals and the crystal morphologies of the fabricated PINFs were examined. PINF-I (lengths = 305 ± 152 nm and diameters = 12 ± 2 nm) was crystallized from crystalline PI dissolved in a concentrated sulfuric acid solution. The resulting PINF-I was isolated from this solution, and it did not aggregate in water. PINF-II with diameters of 105 ± 99 nm was prepared by dispersing PINF-I in a mixed water and t-butanol (TBA) solution (water:TBA = 4:1), followed by freeze-drying. Then, the PINF-II was heated to enhance its crystallinity. X-ray diffraction and transmission electron microscopy studies of the heat-treated PINF-II revealed a PI crystalline unit cell [orthorhombic, a = 1.21 nm, b = 0.88 nm, and c = 2.23 nm (molecular chain axis direction)]. The crystal structure of the heat-treated PINF-II suggested that highly crystalline PINFs were fabricated in which the PI molecular chains were oriented along the direction of the fiber lengths.