The effects of 2 years of storage and 6000 thermocycles on the shear bond strength (SBS) of two self-etching adhesive systems were studied. Two self-etching primer (SEP) systems (Transbond Plus and Beauty Ortho Bond) and one etch and rinse system (Transbond XT) were used to bond brackets to 126 human premolars that were then stored in artificial saliva for 24 hours or 2 years and thermocycled in distilled water before SBS testing with a universal testing machine. The adhesive remnant index (ARI) scores were calculated. Data were compared by two-way analysis of variance and chi-square analysis. Enamel/adhesive interfaces were examined by scanning electron microscopy. There was no significant difference in the mean SBS for the bonding materials among the three conditions. ARI scores showed that Transbond XT and Beauty Ortho Bond had less adhesive remaining on the teeth after ageing compared with storage for 24 hours. Specimens bonded with Beauty Ortho Bond showed leakage between the resin adhesive and enamel after ageing. Both SEP systems produced adequate SBS even after 2 years or 6000 times thermocycling. Thermocycling is an appropriate technique for determining the durability of orthodontic bracket bonding materials.

This study sought to assess the efficacy of two self-etching primer systems (Transbond Plus and Beauty Ortho Bond) on orthodontic brackets. Therefore, shear bond strengths and bracket-adhesive failure modes (ARI scores) were determined and compared against an etch-and-rinse adhesive system (Transbond XT) under two experimental conditions (dry and saliva application). Shear bond strength test was performed at a crosshead speed of 0.5 mm/min, while enamel surfaces and enamel-adhesive interfaces were examined with SEM. There were no significant differences between Transbond XT (9.15 MPa) and Transbond Plus (9.74 MPa) under the dry condition, whereas that of Beauty Ortho Bond (6.47 MPa) was significantly lower than these two systems. Under SEM examination, both self-etching primers showed a milder etching effect and decreased depth of resin penetration into intact enamel than Transbond XT. In conclusion, results of this study showed that both self-etching systems seemed to offer more merits than conventional acid etching because of fewer irreversible changes to enamel.

Orthodontic coated wires with small inner alloy cores withstand less force than expected and may be unsuitable for establishing sufficient tooth movement. The frictional force of coated wires is influenced by total cross-section diameter, inner core diameter, nanohardness, nanoelastic modulus, and elastic modulus.

No abstract

No abstract