LOCA-simulated experiments were performed with MDA, ZIRLOÔ, M5 Ò , NDA, and Zircaloy-2 cladding specimens with local burn-ups ranging from 66 to 76 MWd/kg. Short test rods fabricated with the cladding specimens were heated, isothermally oxidized at 1,459 to 1,480 K in steam flow, and finally quenched in flooding water. Rod rupture and subsequent double-sided oxidation of the cladding were also simulated in the experiments. Neither split-fracture nor fragmentation occurred during the quench in the cladding specimens which were oxidized to about 18-27% of the metallic thickness. Accordingly, the fracture boundary, a most important safety issue, is not reduced significantly by the high burn-up and use of the new alloys within the examined scope, although it may be somewhat reduced with pre-hydriding during the reactor operation as observed in unirradiated specimens.