IntroductionThe aim of this study was to evaluate & compare the wetting ability of five saliva substitutes & distilled water on heat-polymerized acrylic resin. Contact angle of the saliva substitute on denture base can be taken as an indicator of wettability. Good wetting of heat-polymerized acrylic resin is critical for optimum retention of complete dentures.MethodsTwo hundred & forty samples of heat-polymerized acrylic resin were fabricated using conventional method. 240 samples divided into 6 groups with 40 samples in each group. Advancing & Receding contact angles were measured using Contact Angle Goniometer & DSA4 software analysis.ResultsAnova test was carried out to test the significance in difference of contact angle values in the six groups. The mean of advancing angle values & mean of receding angle values of all the six groups has shown statistically significant difference between the groups. The mean of angle of hysteresis values of all the six groups are statistically not significant between the groups. A multiple comparison using Bonferroni’s test was carried out to verify the significance of difference between the contact angles in a pair of groups. Statistically significant difference was seen when Aqwet (Group II) was compared to Distilled water (Group I), Wet Mouth (Group III), E-Saliva (Group IV), Biotene (Group V), and Moi-Stir (Group VI).ConclusionThe contact angles of five saliva substitutes and distilled water were measured and compared. Group II (AQWET) has the lowest advancing and receding contact angle values and the highest angle of hysteresis on heat-polymerized acrylic resin. Based on contact angle values, Group II (AQWET) has the best wetting ability on heat-cured acrylic resins. The ability of saliva to wet the denture surface is one of the most important properties for complete denture retention in dry mouth cases.

Aim:Distortion due to Polymerization shrinkage compromises the retention. To evaluate the amount of retention of denture bases fabricated by conventional, anchorized, and injection molding polymerization techniques.Materials and Methods:Ten completely edentulous patients were selected, impressions were made, and master cast obtained was duplicated to fabricate denture bases by three polymerization techniques. Loop was attached to the finished denture bases to estimate the force required to dislodge them by retention apparatus. Readings were subjected to nonparametric Friedman two-way analysis of variance followed by Bonferroni correction methods and Wilcoxon matched-pairs signed-ranks test.Results:Denture bases fabricated by injection molding (3740 g), anchorized techniques (2913 g) recorded greater retention values than conventional technique (2468 g). Significant difference was seen between these techniques.Conclusions:Denture bases obtained by injection molding polymerization technique exhibited maximum retention, followed by anchorized technique, and least retention was seen in conventional molding technique.