We studied mixed poly(ethylene oxide) (PEO) and poly(2-(dimethylamino)ethyl methacrylate) (PDMAEMA) brushes. The question we attempted to answer was: When the chain grafting points are laterally mobile, how will this lateral mobility influence the structure and phase behavior of the mixed brush? Three different model mixed PEO/PDMAEMA brush systems were prepared: (1) a laterally-mobile mixed brush by spreading onto the air-water interface a mixture of poly(ethylene oxide)-poly(n-butyl acrylate) (PEO-PnBA) and poly(2-(dimethylamino)ethyl methacrylate)-poly(n-butyl acrylate) (PDMAEMA-PnBA) diblock copolymers (the specific diblock copolymers used will be denoted as PEO113-PnBA100 and PDMAEMA118-PnBA100, where the subscripts refer to the number-average degrees of polymerization of the individual blocks), (2) a mobility-restricted (inseparable) version of the above mixed brush prepared using a PEO-PnBA-PDMAEMA triblock copolymer (denoted as PEO113-PnBA89-PDMAEMA120) having respective brush molecular weights matched to those of the diblock copolymers, and (3) a different laterally-mobile mixed PEO and PDMAEMA brush prepared from a PEO113-PnBA100 and PDMAEMA200-PnBA103 diblock copolymer combination, which represents a further more height-mismatched mixed brush situation than described in (1). These three mixed brush systems were investigated by surface pressure-area isotherm and X-ray (XR) reflectivity measurements. These experimental data were analyzed within the theoretical framework of a continuum self-consistent field (SCF) polymer brush model. The combined experimental and theoretical results suggest that the mobile mixed brush derived using the PEO113-PnBA100 and PDMAEMA118-PnBA100 combination (i.e., Mixed Brush System #1) undergoes a lateral macroscopic phase separation at high chain grafting densities, whereas the more height-mismatched system (System #3) is only microscopically phase separated under comparable brush density conditions even though the lateral mobility of the grafted chains is unrestricted. The macroscopic phase separation observed in the laterally-mobile mixed brush system is in contrast to the microphase separation behavior commonly observed in two-dimensional laterally-mobile charged small molecule mixtures. Further study is needed to determine the detailed morphologies of the macro and microphase-separated mixed PEO/PDMAEMA brushes.