We report the fabrication of stretchable sensor films (SSF) using a composite of functionalized polypyrrole- single-walled carbon nanotube (SWCNT)-silver nanowire hybrid networks embedded into a cross-linked polydimethylsiloxane elastomer. The SSF exhibited low resistivity of 30 Ω/sq and an outstanding mechanical elasticity of up to 25% (no visible change in the sheet resistance after 100 cycle at stretching-release test of 25%). These SSFs were responsive to 1 ppm ammonia gas even at a low temperature of 40 °C with 20% relative humidity and also maintained reproducibility and reversibility when repeatedly exposed to ammonia gas more than 100 times. In addition, it was confirmed that the sensor film was hardly affected even at a relative humidity range of 20% to 80%.

Core–shell nanorod composites with a SWCNT in core and PPy/PA shells, SWCNT@PPy@PA, for 100 ppb ammonia gas sensing.

We report the fabrication of stretchable transparent electrode films (STEF) using 15-nm-diameter Ag nanowires networks embedded into a cross-linked polydimethylsiloxane elastomer. 15-nm-diameter Ag NWs with a high aspect ratio (˃1000) were synthesized through pressure-induced polyol synthesis in the presence of AgCl particles with KBr. These Ag NW network-based STEF exhibited considerably low haze values (<1.5%) with a transparency of 90% despite the low sheet resistance of 20 Ω/sq. The STEF exhibited an outstanding mechanical elasticity of up to 20% and no visible change occurred in the sheet resistance after 100 cycles at a stretching-release test of 20%.

No abstract