The mesomorphic isotactic polypropylene was prepared by rapid compression instead of the common method of temperature quenching, and their phase transition under high pressure was investigated in depth by combining wide‐angle X‐ray diffraction, small‐angle X‐ray scattering, and differential scanning calorimetry techniques. It was found that annealing under pressure can promote the further arrangement of chain segments of the mesophase toward the crossed state in the orthorhombic γ‐phase, and the long period of the mesophase slightly decreased from 8.2 to 7.2 nm. The kinetics of this meso‐γ transition strongly depends on pressure. As annealing pressure increased, the mobility of molecular segments was reduced, and then the onset and finishing time of phase transition were both delayed significantly. A critical annealing pressure was found between 1.6 and 1.75 GPa, which determines whether the phase transition occurs or not. When pressure reaches 1.75 GPa, mesophase did not transform at all within 120 min. Based on the results, a reasonable mechanism was proposed to show the crystallization process of mesophase under high‐pressure annealing. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2019, 57, 651–661

Isotactic polypropylene filled with 1 wt.% multi-walled carbon nanotubes (iPP/MWCNTs) were prepared, and their crystallization behavior induced by pressurizing to 2.0 GPa with adjustable rates from 2.5 to 1.3 × 104 MPa/s was studied. The obtained samples were characterized by combining wide angle X-ray diffraction, small angle X-ray scattering, differential scanning calorimetry, transmission electron microscopy and atomic force microscopy techniques. It was found that pressurization is a simple way to prepare iPP/MWCNTs composites in mesophase, γ-phase, or their blends. Two threshold pressurization rates marked as R1 and R2 were identified, while R1 corresponds to the onset of mesomorphic iPP formation. When the pressurization rate is lower than R1 only γ-phase generates, with its increasing mesophase begins to generate and coexist with γ-phase, and if it exceeds R2 only mesophase can generate. When iPP/MWCNTs crystallized in γ-phase, compared with the neat iPP, the existence of MWCNTs can promote the nucleation of γ-phase, leading to the formation of γ-crystal with thicker lamellae. If iPP/MWCNTs solidified in mesophase, MWCNTs can decrease the growth rate of the nodular structure, leading to the formation of mesophase with smaller nodular domains (about 9.4 nm). Mechanical tests reveal that, γ-iPP/MWCNTs composites prepared by slow pressurization display high Young’s modulus, high yield strength and high elongation at break, and meso-iPP/MWCNTs samples have excellent deformability because of the existence of nodular morphology. In this sense, the pressurization method is proved to be an efficient approach to regulate the crystalline structure and the properties of iPP/MWCNTs composites.

Habitat quality is a key indicator for assessing the biodiversity-maintenance functions of ecosystem services. The issue of habitat quality changes in semi-arid and arid areas has been becoming serious, but there are few deep investigations of habitat quality in these regions, such as studies of the temporal and spatial changes of habitat quality and its driving forces. This study focuses on the agro-pastoral ecotone of northern Shaanxi with vulnerable biodiversity. By using the Fragstats software, the InVEST model, and the Geo-detector model, we analyzed land-use data collected from 1990, 2000, 2010, and 2020, and we explored the landscape pattern index, the spatial and temporal variation of habitat quality, and the influence of its drivers. GDP, population density, precipitation, temperature, land use, NDVI, elevation, and slope were detected by Geo-detector. The research results show that: (1) Arable land and grassland were the dominant land types from 1990 to 2020, and there was significant mutual circulation between arable land and grassland. Forest area increased by 24%. Many other land-use types were transformed into construction land, and construction land increased by 727% compared with the base period. (2) Landscape heterogeneity increased in the study region, shown by the fractured structure of the overall landscape and by the aggravated human disturbance of the landscape. (3) Average habitat quality underwent a trend of oscillation. Regarding spatial distribution, habitat quality was higher in the east than in the west. (4) The influencing factors of habitat quality monitored by Geo-detectors show that the driving force of land use on habitat quality was the strongest, followed by precipitation and vegetation coverage. Elevation, slope, GDP, and population density had the least influence on habitat quality. The bi-factor interaction enhanced habitat quality to different levels. This study is critical to the conservation of biodiversity and to ecological civilization construction in arid and semi-arid regions.

Using a homemade pressure device, we explored the synergistic effect of pressurization rate and β-form nucleating agent (β-NA) on the crystallization of an isotactic polypropylene (iPP) melt. The obtained samples were characterized by combining small angle X-ray scattering and synchrotron wide angle X-ray diffraction. It was found that the synergistic application of pressurization and β-NA enables the preparation of a unique multi-phase crystallization of iPP, including β-, γ- and/or mesomorphic phases. Pressurization rate plays a crucial role on the formation of different crystal phases. As the pressurization rate increases in a narrow range between 0.6–1.9 MPa/s, a significant competitive formation between β- and γ-iPP was detected, and their relative crystallinity are likely to be determined by the growth of the crystal. When the pressurization rate increases further, both β- and γ-iPP contents gradually decrease, and the mesophase begins to emerge once it exceeds 15.0 MPa/s, then mesomorphic, β- and γ- iPP coexist with each other. Moreover, with different β-NA contents, the best pressurization rate for β-iPP growth is the same as 1.9 MPa/s, while more β-NA just promotes the content of β-iPP under the rates lower than 1.9 MPa/s. In addition to inducing the formation of β-iPP, it shows that β-NA can also significantly promote the formation of γ-iPP in a wide pressurization rate range between 3.8 to 75 MPa/s. These results were elucidated by combining classical nucleation theory and the growth theory of different crystalline phases, and a theoretical model of the pressurization-induced crystallization is established, providing insight into understanding the multi-phase structure development of iPP.

No abstract