Rice husk ash (RHA) was used as a reinforcing filler in epoxidized natural rubber (ENR) with various loading levels (0, 10, 20, and 30 phr), and silica filled ENR was also studied for comparison. The effects of RHA content on cure characteristics, mechanical properties, dynamic mechanical properties, and thermoelastic behavior of the filled ENR composites were investigated. It was found that the incorporation of RHA significantly affected the cure characteristics and mechanical properties. That is, the incorporation of RHA caused faster curing reactions and increased Young's modulus and tensile strength relative to the unfilled compound. This might be attributed to the metal oxide impurities in RHA that enhance the crosslinking reactions, thus increasing the crosslink density. Further improvements in the curing behavior and the mechanical properties of the filled composites were achieved by in situ silanization with bis(triethoxysilylpropyl) tetrasulfide (Si69). It was found that the rubber-filler interactions reinforced the composites. This was indicated by the decreased damping characteristic (tan ) and the other changes in the mechanical properties. Furthermore, the ENR composites with Si69 had improved filler dispersion. Temperature scanning stress relaxation (TSSR) results suggest that the metal oxide impurities in RHA promote degradation of the polymer network at elevated temperatures.

Rice husk ash (RHA) and siliceous earth (SE) were compared as alternative reinforcing fillers in epoxidized natural rubber (ENR) vulcanizates. The effects of RHA and SE on processability, curing characteristics, mechanical, thermal and morphological properties, and thermoelastic behavior of vulcanizates were studied, in the presence and absence of bis(triethoxysilylpropyl) tetrasulfide (TESPT) silane coupling agent. The results indicated that the RHA offers processing advantages over the commercial SE. The filled ENR vulcanizates without TESPT provided higher tensile strengths than the unfilled ENR vulcanizates, but had lower elongations at break. This is attributed to physical interactions between filler particles and rubber matrix, which affects the reinforcement by the filler. The modification of filler surfaces with TESPT resulted in further improved properties of the rubber vulcanizates. This is attributed to the coupling of polymer matrix and filler particles via TESPT linkages that increased the polymer–filler interactions. It was also found that the RHA filler, a renewable resource, exhibited similar reinforcement to the conventional SE. This indicates that the RHA has great potential as a reinforcing filler that can substitute for conventional SE in polymer composites. POLYM. COMPOS., 39:414–426, 2018. © 2016 Society of Plastics Engineers

No abstract

No abstract

This article aims to study the influences of the selective location of rice husk ash (RHA) particles on morphological, mechanical, and dynamic properties of epoxidized natural rubber and thermoplastic polyurethane blends (ENR/TPU). Thermodynamic aspects, that is, interfacial tension and work of adhesion were assessed from estimates based on surface tension. It was found that the RHA particles had stronger interactions with the ENR than the TPU, of the co‐continuous phases. The phase structure was mainly controlled by kinetic factors, particularly by the mixing sequence, and to a lesser degree by thermodynamics. Furthermore, the microstructure with RHA particles dispersed in the ENR co‐continuous phase was found to give enhanced mechanical properties. This might be attributed to the higher work of adhesion between ENR and RHA that stabilized the encapsulated RHA particles against shear and elongational stresses, during melt mixing and in the final products. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2018, 135, 46681.