The protein fouling phenomenon was investigated on modified polysulfone ultrafiltration membranes. The sulfonation degree was correlated to the extent of deposition of bovine serum albumin. It was shown that membranes prepared from modified polysulfone were less fouled than their off-charge analogues. The fouling phenomenon was also investigated for membranes prepared from co-cast blends. It was demonstrated that blends containing more than 50 wt.4'0 of sulfonated derivative behaved like a membrane from pure sulfonated polysulfone. The effect was attributed to surface separation of polymers and formation of surfaces enriched with sulfonic groups. ZUSAMMENFASSUNG:An sulfonierten Polysulfon-Ultrafiltrationsmembranen wurde das Problem des Foulings untersucht. Der Sulfonierungsgrad wurde mit dem AusmaB der Deposition von Rinderserumalbumin korreliert. Es zeigte sich, da8 sich Membranen aus modifiziertem Polysulfon weniger zusetzten als ihre nichtmodifizierten Analoga. Membranen aus Blends von modifiziertem mit nicht modifiziertem Polysulfon wurden ebenfalls untersucht, wobei sich solche aus Blends mit einem Anteil von mehr als 50 Gew.-Vo sulfoniertem Polysulfon wie solche aus reinem sulfoniertem Polysulfon verhielten. Dies wird darauf zuruckgefuhrt, da8 sich bei der Herstellung der Blend-Membranen sulfoniertes Polysulfon an der OberflBche anreichert.

No abstract

No abstract