The cathode material, high Nickel content Ni0.7Co0.2Mn0.1 (NCM), was synthesized by coprecipitation with NH4OH used as a complexing agent. The prepared materials are made in the formation of spherical particles of Li(Ni0.7Co0.2Mn0.1)O2 of several micrometers in diameter. Al2O3 was coated by an impregnation method and its content was gradually increased to 1, 2 and 5 wt%. As a result, 1 wt% coated Al2O3 compared to pristine NCM exhibited 82% and 80% retention rates at 5 C and 1 wt% Al2O3 coated NCM recovery at 0.2 C after 5 C showed 100%. In addition, capacity retention of 1 wt% NCM+Al gently decreased in 100 cycle life characteristics, and capacity retention of 95% or more was confirmed.

It is important to prevent vapor explosion for steel mill industries for the reason that explosions can produce overpressure which cause buildings and facilities to rupture.The spontaneous vapor explosion occurs when a molten slag contacts with coolant.In this research, the molten slag which includes more than 10 chemical compositions produced in actual steel mill industries is employed. Three types of coolant were