Size effect on the structural, magnetic, and magnetotransport properties of electron doped manganite La0.15Ca0.85MnO3

A silica-colloidal template approach was used to prepare monodisperse nanospheres of TiO2. Close-packed arrays of silica spheres were infiltrated with a sucrose precursor used as a source of carbon. The infiltrated sucrose was carbonized by calcination at 800 °C in flowing argon. After removal of the silica spheres by washing with HF, a porous carbon replica remained. The resulting pores in the replica were then filled with a chloroform solution of titanium alkoxide. Nanospheres of TiO2 approximately 200 nm in diameter were obtained after calcination of the organic component at 600 °C in an argon atmosphere and subsequent sintering in air at 700 °C.