The influence of pre-strain on low cycle fatigue behavior of Fe-18Mn-0.05Al-0.6C TWIP steel was studied by conducting axial strain-controlled tests. As-received plates were deformed by rolling with reduction ratios of 10 and 30%, respectively. A triangular waveform with a constant frequency of 1 Hz was employed for low cycle fatigue test at the total strain amplitudes in the range of ±0.4 ∼ ±0.6 pct. The results showed that low-cycle fatigue life was strongly dependent on the amount of pre-strain as well as the strain amplitude. Increasing the amount of prestrain, the number of reversals to failure was significantly decreased at high strain amplitudes, but the effect was negligible at low strain amplitudes. A new model for predicting fatigue life of pre-strained body has been suggested by adding ΔE pre-strain to the energy-based fatigue damage parameter. Also, high-cycle fatigue lives predicted using the low-cycle fatigue data well agreed with the experimental ones.

Abstract：In this study, the reflection of the L(0,2), axially symmetric guided elastic wave from defects in pipes above ground is examined using finite element method. Phase and group velocity dispersion curves for the pipe were presented for the selection of the excitation mode. Some simple signal processing was applied to determine the amplitude of each of the reflected waves and to calculate the reflection coefficient. The results show the reflection coefficient of this mode is very close to a linear function of the circumferential extent of the defect. The motivation for the work was the development of a technique for inspecting chemical plant pipelines, but the study addresses the nature of the reflection function and its general applicability.