The adhesion properties of epoxidized natural rubber (ENR 25)/(ethylene‐propylene‐diene rubber) blend adhesive were investigated by using various blend ratios of the two rubbers and rate of testing. Coumarone‐indene resin was used as the tackifier. Results show that the loop tack and peel strength of adhesives increase steadily up to 60% ENR 25 before decreasing with further increase in % ENR 25. This observation is attributed to an increase in wettability and compatibility up to the optimum value of the ENR 25 blend ratio. However, shear strength increases continuously with increasing percentage of ENR 25, an observation that is ascribed to the increasing cohesive strength of the blend adhesive. In all cases, the adhesion properties increase with increasing coating thickness and testing rates. J. VINYL ADDIT. TECHNOL., 22:134–139, 2016. © 2014 Society of Plastics Engineers

The effect of zinc oxide and testing rate on tack, peel strength, and shear strength of styrene‐butadiene rubber (SBR)/standard Malaysian rubber (SMR L) blend adhesive was investigated using coumarone‐indene resin and toluene as the tackifying resin and solvent, respectively. Zinc oxide concentration was varied from 0–50 parts per hundred parts of rubber (phr). A Lloyd Adhesion Tester operating from 10–60 cm/min was used to determine the adhesion property. Results show that tack and peel strength increases with zinc oxide concentration up to 20 phr of the filler loading. This observation is attributed to the varying degree of wettability, which culminates at 20 phr of zinc oxide content. For the shear strength, it increases steadily with zinc oxide loading, an observation that is associated to the steady increase in cohesive strength due to the interaction between the adhesive and the filler. The adhesion property increases with testing rate and coating thickness. J. VINYL ADDIT. TECHNOL., 22:3–7, 2016. © 2014 Society of Plastics Engineers

No abstract

The loop tack, peel strength, and shear strength of crosslinked epoxidized natural rubber (ENR 25)/ethylene-propylene-diene rubber (EPDM) blend adhesives were investigated. Coumarone-indene resin, toluene, and benzoyl peroxide were used as the tackifier, solvent, and crosslinking agent, respectively, throughout the experiment. The adhesive was coated on a polyethylene terephthalate (PET) substrate using a SHEEN hand coater at 60 μm and 120 μm coating thickness. It was cured at 80°C for 30 minutes before testing on a Lloyd adhesion tester operating at testing rates from 10 to 60 cm min−1. Results show that loop tack and peel strength of the ENR 25/EPDM adhesive pass through a maximum value at 2 parts per hundred parts of rubber (phr) of benzoyl peroxide content. This observation is attributed to the increase in crosslinking which enhances the cohesive strength of the adhesive. Further addition of the crosslinking agent decreases the tack and peel strength due to the decrease in wettability of the over-crosslinked adhesive. Shear strength, however, increases steadily with benzoyl peroxide content, an observation which is associated with the steady increase in the cohesive strength. The adhesion properties increase with increasing coating thickness and testing rate.