X-ray diffraction (XRD) patterns were calculated and compared to literature data with the aim of investigating the crystal structure of nanocrystalline calcium silicate hydrates (C-S-H), the main binding phase in hydrated Portland cement pastes.

No abstract

No abstract

No abstract

The structure of nanocrystalline calcium silicates hydrates (C–S–H) having Ca/Si ratios ranging between 0.57 ± 0.05 and 1.47 ± 0.04 was studied. All samples are nanocrystalline and defective tobermorite. An increase of the Ca/Si ratio resulting from omission of bridging Si in the Si chains and incorporation of interlayer Ca was observed.