Thermoplastic resin matrix has a high melt viscosity, which is difficult to impregnate with fibers. The addition of flame retardant will further increase the viscosity of the melt and increase the difficulty of impregnation. It is possible to reduce the effect of flame retardant on melt viscosity by adding high-flow polypropylene. In this study, the effect of adding flame retardant on the impregnation quality of prepreg tape was investigated. By adding high-flow polypropylene to improve the melt viscosity of flame-retardant-modified polypropylene, continuous glass-fiber-reinforced polypropylene flame-retardant prepreg tape was successfully prepared. Intumescent flame retardant (IFR) was added at 20 wt%, 25 wt%, 30 wt% of the polypropylene matrixes, which were prepared by melt impregnation. The composites were analyzed with thermogravimetric analysis, limiting oxygen index testing, UL-94 flame retardancy testing, cone calorimeter testing (CCT) and scanning electron microscopy. Tests involving the flame retardant showed that when the added amount of flame retardant reached 25%, the UL-94 flame retardancy grade reached V0. Compared with the CCT sample heating data, taking economic considerations into account, 25 wt% IFR addition was the most suitable.

Multifunctional composite panels for flame retardant and thermal insulation have not yet been studied. In the current study, we prepared sandwich sheets by using continuous glass fiber flame retardant polypropylene prepreg tape and compared the thermal insulation properties of different fillings. Corrugated sandwich panels, featuring a corrugated space filled with different materials, were prepared and their thermal and mechanical properties are tested and verified. Determining the two structural parameters that have the greatest influence on the heat transfer performance of corrugated sandwich panels has important guiding significance for the structural design of corrugated panels.