The effect from thickness of an intermediate copper layer in nanosized Fe 50 Pt 50 (15 nm) / Cu (x) / Fe 50 Pt 50 (15 nm) (x = 7.5, 15, and 30 nm) composite films on SiO 2 (100 nm) / Si(001) substrates on the diffusion-controlled phase formation processes-transformation of the disordered magnetically soft A1(FePt) phase into the ordered magnetically hard L1 0 (FePt) phase during annealing in vacuum-is studied by physical materials science methods: X-ray diffraction and measurement of magnetic properties. The A1(FePt) phase forms in all films during deposition. Annealing in vacuum in the temperature range 300-900ºC is accompanied by thermally activated diffusion processes between the Cu and FePt layers. When thickness of the intermediate Cu layer increases from 7.5 nm up to 15 nm, the onset temperature of A1(FePt) L1 0 (FePt) phase transformation raises by 100°C, i.e., to 800°C. Simultaneously, the coercivity in films decreases since Cu dissolves in the FePt lattice.
Оттиски доступны непосредственно от издателя Фотокопирование разрешено только в соответствии с лицензией 2014 ИМФ (Институт металлофизики им. Г. В. Курдюмова НАН Украины) Напечатано в Украине.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.