An Al-Si coating was prepared on IC21 alloy by powder pack cementation. The cyclic oxidation tests were carried out at 1150 in air for up to 100 h. The results indicate that the oxidation resistance of IC21 alloy is significantly improved by the Al-Si coating due to the presence of Ni2Al3and β-NiAl enriched outer layer, and Si can effectively supress the outward diffusion of Mo. The oxide scales mainly consist of α-Al2O3, which is the favorite to the oxidation resistance. Phase transformation occurred from β-NiAl to γ-Ni3Al and γ-Ni in the coating during oxidation. The coating still remained a certain amount of β phase after oxidation for 100h, which indicate a good protection. The microstructure change evolution was characterized, and the oxidation behavior of the coating was discussed.

Storage tank is an essential vessel in petrochemical industry, and the corrosion of tank is an important reason for the safety hazard. The corrosion of tank bottom plate is more serious than the tank wall, and it is not easy to check and repair, when damaged to a certain extent it will cause the leakage of the media, then lead to waste of energy, environmental pollution, at the same time it will cause a major accident. Magnetic flux leakage testing is widely used in the field of tank floor inspection with the advantages of fast scanning speed, accurate results and so on. In this paper, the finite element simulation and analysis of the corrosion defect leakage magnetic field is used to obtain the data, and the characteristic of the leakage magnetic field is extracted. The effect of defect depth and width and shape on the magnetic flux leakage field is studied, and the distribution curve of the magnetic flux leakage field is obtained.