In the present work, two successive magneto-structural transformations (MSTs) consisting of martensitic and intermartensitic transitions have been observed in polycrystalline Ni55.8Mn18.1Ga26.1 Heusler alloy. Benefiting from the additional latent heat contributed from intermediate phase, this alloy exhibits a large transition entropy change ΔStr with the value of ~27 J/kg K. Moreover, the magnetocaloric effect (MCE) has been also evaluated in terms of Maxwell relation. For a magnetic field change of 30 kOe, it was found that the calculated value of refrigeration capacity in Ni55.8Mn18.1Ga26.1 attains to ~72 J/kg around room temperature, which significantly surpasses those obtained for many Ni-Mn based Heusler alloys in the same condition. Such an enhanced MCE can be ascribed to the fact that the isothermal entropy change ΔST is spread over a relatively wide temperature interval owing to existence of two successive MSTs for studied sample.

We report a detailed study of two successive first-order transitions, including a martensitic transition (MT) and an antiferromagnetic (AFM)-ferromagnetic (FM)-like transition, in Mn1-xFexNiGe (x = 0, 0.06, 0.11) alloys by X-ray diffraction, differential scanning calorimetry, magnetization and linear thermal expansion measurements. Such an AFM-FM-like transition occurring in the martensitic state has seldom been observed in the M(T) curves. The results of Arrott plot and linear relationship of the critical temperature with M2 provide explicit evidence of its first-order magnetoelastic nature. On the other hand, their performances as magnetocaloric and negative thermal expansion materials were characterized. The isothermal entropy change for a field change of 30 kOe reaches an impressive value of −25.8 J/kg K at 203 K for x = 0.11 compared to the other two samples. It demonstrates that the magneto-responsive ability has been significantly promoted since an appropriate amount of Fe doping can break the local Ni-6Mn AFM configuration. Moreover, the Fe-doped samples reveal both the giant negative thermal expansion and near-zero thermal expansion for different temperature ranges. For instance, the average thermal expansion coefficient ā of x = 0.06 reaches −60.7 × 10−6/K over T = 231–338 K and 0.6 × 10−6/K over T = 175–231 K during cooling.

In this work, we have developed a ferromagnetic shape memory alloy Co50V34Ga16 with a metamagnetic martensitic transformation (MT) from the high-magnetization austenitic phase to the low-magnetization martensitic phase. As a consequence of a strong coupling between structure and magnetic degrees of freedom, the metamagnetic MT of this alloy is relatively sensitive to the external magnetic field, thus giving rise to a field-induced reverse MT. Associated with such a unique behavior, both considerable inverse magnetocaloric effect (9.6 J/kg K) and magnetostrain (0.07%) have also been obtained under the magnetic field change of 3 T. Our experimental results indicate that this kind of Co-V based alloy probably becomes an alternatively promising candidate for applications in magnetic sensors and magnetic refrigeration.

No abstract