The interface chemistry and evolution of the evaporated perovskite films on ITO, pedot/ITO, Si and glass substrates are studied. As evidenced by X-ray diffraction and X-ray photoemission spectroscopy (XPS) results, the PbI2 phase is found to be inevitably formed at the very initial growth stage, even under the conditions of a MAI-rich environment. The extremely low binding energy of adsorbed MAI particles on all the above substrates, as compared to that of PbI2 particles, is responsible for the presence of the PbI2 phase at the interface. The formation of both hole and electron barriers at the interface of PbI2/MAPbI3, as evidenced by XPS measurements, could block carrier transport into the electrode and thus deteriorate solar cell performance. This result reveals the origin of the poor performance of perovskite solar cells (PSCs) by the vacuum evaporation method, and may help to improve the performance of PSCs made using the vacuum evaporation method.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.