The influence of time and temperature of ageing on the σ-phase morphology in ferritic-austenitic cast steel have been investigated in this study. The morphology and quantity of the σ-phase were analyzed by using optical microscope, X-ray diffractometry, scanning electron microscope and image analysis, respectively. The annealing temperature has a significant influence on the morphology, volume fraction and the dynamics of σ-phase precipitation. Surface development of the σ-phase decreases from R=4.3, for the cast steel annealed at 700°C to R=2.4 for the cast steel annealed at 900°C, and the volume fraction Vvσ from 50.8% to 26.5%, respectively. The most rapid progress of δ → σ + γ’ transformation was observed at 800°C.

UD C 539. 4 M ic r o s t r u c t u r a l a n d F r a c t u r e A n a ly s i s o f A g e d C a s t D u p le

The paper presents the results of examination concerning optimization of the σ phase precipitates with respect to the functional properties of ferritic-austenitic cast steel. The examined material comprised two grades of corrosion-resistant cast steel, namely GX2CrNiMoN25-6-3 and GX2CrNiMoCuN25-6-3-3, used for example in elements of systems of wet flue gas desulphurisation in power industry. The operating conditions in media heated up to 70°C and containing Cland SO 4 ions and solid particles produce high erosive and corrosive wear. The work proposes an application of the σ phase as a component of precipitation strengthening mechanism in order to increase the functional properties of the material. Morphology and quantities of σ phase precipitates were determined, as well as its influence on the erosion and corrosion wear resistance. It was shown that annealing at 800°C or 900°C significantly improves tribological properties as compared with the supersaturated state, and the best erosion and corrosion wear resistance achieved due to the ferrite decomposition δ → γ' + σ was exhibited in the case of annealing at the temperature of 800°C for 3 hours.

The examined material comprised two grades of corrosion-resistant cast steel, namely GX2CrNiMoN25-6-3 and GX2CrNiMoCuN25-6-3- 3, used for example in elements of systems of wet flue gas desulphurisation in power industry. The operating conditions in media heated up to 70°C and containing Cl' and SO4 ions and solid particles produce high erosive and corrosive wear.The work proposes an application of the σ phase as a component of precipitation strengthening mechanism in order to increase the functional properties of the material. The paper presents the results of examination of the kinetics of σ phase precipitation at a temperature of 800°C and at times ranging from 30 to 180 minutes. Changes in the morphology of precipitates of the σ phase were determined using the value of shape factor R. Resistance to erosion-corrosion wear of duplex cast steel was correlated with the kinetics of sigma phase precipitating.