A B S T R A C T Tension-compression and rotating-bending fatigue tests were carried out using aluminium alloy 2024-T3, in 3% NaCl solution. The corrosion pit growth characteristics, and also the fatigue crack initiation and propagation behaviour were investigated in detail. The results obtained are summarized as follows: (i) Most of corrosion fatigue life (60-80%) is occupied with a period of corrosion pit growth at low-stress amplitude. The corrosion pit growth law can be expressed as functions of stress amplitude σ a and an elapsed time t. (ii) The critical stress intensity factor for crack initiation from the corrosion pit was determined as 0.25 MPa √ m. This value is the same as the threshold stress intensity factor range for crack propagation. (iii) Corrosion fatigue life can be estimated on the basis of corrosion pit growth law and crack propagation law. The estimated fatigue lives agree well with the experimental data.
scite is a Brooklyn-based organization that helps researchers better discover and understand research articles through Smart Citations–citations that display the context of the citation and describe whether the article provides supporting or contrasting evidence. scite is used by students and researchers from around the world and is funded in part by the National Science Foundation and the National Institute on Drug Abuse of the National Institutes of Health.