The results of experimental studies of the phase transformation in composite films of the Se-Cu system obtained in vacuum as a result of the sequential thermal deposition of selenium and copper on a glass substrate are presented. At a fixed thickness of the selenium layer (45 nm), the effect of the thickness of the copper layer (40 - 115 nm) on the phase composition of the synthesized films formed as a result of explosive crystallization occurring during the interaction of hot copper clusters with low-melting selenium was studied. It was found that the subsequent thermal annealing of the synthesized films is accompanied by a significant change in their phase composition and optical transmission spectra.

Представлены результаты экспериментальных исследований фазового превращения в композитных пленках системы Se-Cu, полученных в вакууме в процессе последовательного термического осаждения селена и меди на стеклянную подложку. При фиксированной толщине слоя селена (45 нм) исследовалось влияние толщины слоя меди (40-115 нм) на фазовый состав синтезированных пленок, формируемых в процессе взрывной кристаллизации, происходящей при взаимодействии горячих кластеров меди с легкоплавким селеном. Установлено, что последующий термический отжиг синтезированных пленок сопровождается существенным изменением их фазового состава и спектров оптического пропускания. Ключевые слова: фазовые превращения, композитные пленки системы Se-Cu, взрывная кристаллизация, термический отжиг, оптические свойства.