− In this study, we investigated the effectiveness of an ultrasonic nanocrystal surface modification (UNSM) technique on the mechanical and wear properties of tungsten carbide (WC). The UNSM technique is a newly developed surface modification technique that increases the mechanical properties of materials by severe plastic deformation. The objective of this study was to improve the wear resistance of press die made of WC by applying the UNSM technique. We observed the microstructures of the untreated and UNSM-treated specimens using a scanning electron microscope (SEM), and energy-dispersive X-ray spectroscopy (EDX) was used to investigate the chemical composition. The SEM observations showed the pore size and the number of pores decreased after the UNSM treatment. We assessed the wear behavior of both the untreated and UNSM-treated specimens using a scratch test. The test results showed that the wear resistance of the UNSM-treated specimens increased by about 46% compared with the untreated specimens. This may be attributed to increased hardness, reduced surface roughness, induced compressive residual stress, and refined grain size following the application of the UNSM technique. In addition, we found that the UNSM treatment increased the carbon concentration to 63% from 33%. We expect that implementing the findings of this study will lead to an increase in the life of press dies.Keywords − dimple(딤플), press die(프레스 금형), sintered tungsten carbide(초경), surface hardness(표면경도), ultrasonic nanocrystal surface modification(초음파나노표면개질)

− In this study, we apply an ultrasonic nanocrystal surface modification (UNSM) technique to radial journal bearings (JBs) and disks made of SUJ2 and SCM440, respectively. We investigate frictional properties of untreated and UNSM-treated specimens using a ball-on-disk tester. We construct the Stribeck curve at the boundary, under mixed and full hydrodynamic lubrication conditions for the specimens using friction data obtained from JB tests. The friction at the boundary lubrication condition and the transition period to mixed lubrication condition on the UNSM-treated specimens is reduced, which improves the service life of JBs. The major effects of this reduction in the three lubrication regimes can be explained in the terms of improved mechanical properties and the presence of micro dimples. Moreover, we estimate the friction and fatigue properties of SCM440 specimens using a ball-on-disk specimen under dry and oil-lubricated conditions. Friction test results reveal that the UNSM-treated specimens show lower friction coefficient than the untreated specimens under both dry and oil-lubricated conditions. We evaluate the fatigue properties of SCM440 specimens by calculating the Hertzian stress with respect to the failure cycles. Fatigue tests results also reveal that the UNSM-treated specimens possess a longer fatigue life than the untreated specimens. The improved properties are effective in increasing the energy efficiency of bearings.