The novel carbon coating process for interlayer of fiber reinforced ceramic composites between fiber and matrix was performed by carbonizing phenolic resin solution that coated on fiber surface in N 2 atmosphere at 600 o C to improve the strength and fracture toughness of CMC(ceramic matrix composite). 160 nm carbon layer was coated on fiber surface with 5 vol% of phenolic resin solution. Since the process temperature (600 o C) is lower than chemical vapor deposition(900~1000 o C), the strength and toughness could be preserved. Furthermore the coating thickness uniformity was improved to 8% of deviation along the stacking sequence. Therefore, prevention from fiber degradation during coating process and controlling coating thickness uniformity along the preform depth were achieved by coating with phenolic resin carbonizing method.

No abstract

The need of reusing sewage sludge is highly increasing as the amount of domestic sewage sludge is growing and sewage management strategies were reinforced. Accordingly, in this research, we studied the composting possibility of sludge in sewage treatment plant J, using dryer facility with indirect system by conducting component analysis of dried sludge and experiment on cultivating crops. It was observed from the component analysis, that the dried sludge is appropriate for both decomposed manure standard of Ministry of Environment and fertilizer standard of Rural Development Administration. Besides, in the experiment on cultivating lettuce, the experimental group(soil + dried sludge) was superior to the control group(soil + bed soil) in apparent condition of leaves tensity and damage by disease and pest. In case of cultivating tomato, the experimental group showed stronger durability of fruits dangling on stems compared to the control group after 9 weeks. Consequently, the excess sludge dried by indirect heating system in the sewage treatment plant J is appropriate for the standard of both Ministry of Environment and Rural Development Administration and show good result in experiment on cultivating crops therefore it can be reused for composting.

In this study, we investigated the mechanical behavior of carbon fiber reinforced silicon carbide composites by indentation stress. Relatively porous and dense fiber reinforced ceramic composites were fabricated by liquid silicon infiltration (LSI) process. Densification of fiber composite was controlled by hardening temperature of preform and consecutive LSI process. Load-displacement curves were obtained during indentation of WC sphere on the carbon fiber reinforced silicon carbide composites. The indentation damages at various loads were observed, and the elastic modulus were predicted from unloading curve of load-displacement curve.